Electronics Forum | Tue Apr 09 05:36:27 EDT 2002 | lhudson1
Silver in the paste is present to minimise any negative effects of silver in the pcb finish or component terminations. 2% Ag prevent silver leaching thus giving a more reliable joint.
Electronics Forum | Tue Apr 09 00:26:46 EDT 2002 | craigj
Are currently investigating a change of solder paste for various reasons and are considering a move from 63/37 to using 2% silver solder paste for increased long term reliabilty of solder joints with gold finish PCBs and to further reduce reflow temp
Electronics Forum | Fri Aug 13 16:54:20 EDT 2004 | davef
If the terminations on your components are not barrier plated, you must be very careful about the amount of time you stay above liquidous. As you'd expect, longer is not better. The longer you stay at liquidous, the more of the component terminatio
Electronics Forum | Thu Apr 20 14:08:34 EDT 2006 | cw
hi All, recently i have received some parts with the lead turning black, and i then found out the leads are silver plating, is that going to be a problem? or it is simply a cosmetic issue? pls advise ASAP!! thansk a lot!!
Electronics Forum | Thu Oct 18 18:39:15 EDT 2001 | davef
Responding to your questions ... RELIABILITY OF 1% SILVER SOLDER PASTE: It�s as good as the next solder paste, all other things the same. Look at your back articles by Jennie Hang in SMT magazine. I want to say she wrote an article on the topic i
Electronics Forum | Thu Apr 20 14:11:24 EDT 2006 | cw
hi All, recently i have received some parts with the lead turning black, and i then found out the leads are silver plating, is that going to be a problem? or it is simply a cosmetic issue? pls advise ASAP!! thansk a lot!!
Electronics Forum | Thu Apr 20 17:16:02 EDT 2006 | GS
Silver tarnish on lead could compromise the soldering, mainly in case of No Clean process. Make sure components are correctly packaged and stored. Check the vintage ( Manufacturing Data Code) and in order to avoid them to get old on shelf make sure F
Electronics Forum | Wed Apr 26 10:27:37 EDT 2006 | slaine
weve hand soldered a few components that were tarnished with no problems, also the tarnish is electrically conductive if it helps.
Electronics Forum | Tue Apr 13 09:11:54 EDT 1999 | Dave F
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Tue Apr 13 17:44:29 EDT 1999 | Christopher Lampron
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to