Electronics Forum | Tue May 16 15:30:07 EDT 2006 | George
Hi John, Are you talking about cleaning the pallets after running to store them? or during production? well in any case...I recently started to use this cleaning solution "Cybersolv" from Kyzen. It is water soluble and also can be used instead of IP
Electronics Forum | Tue May 16 11:58:27 EDT 2006 | jsloot
What is the best or ideal cleaning method for wave solder pallets? I have been using iso prop and am not sure if this is the cause for having brittle wall material. I wouldn't think alcohol would degrade the durastone material. Most of my pallets hav
Electronics Forum | Tue May 16 22:30:19 EDT 2006 | davef
Check the fine SMTnet Archives. For instance: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=5386
Electronics Forum | Mon May 14 10:44:57 EDT 2007 | realchunks
Hi D0m, What material are they made of?
Electronics Forum | Wed May 16 09:12:58 EDT 2007 | d0min0
carriers / frames are made of CAS761 and some of Contaval
Electronics Forum | Wed May 16 12:11:03 EDT 2007 | slthomas
Is the frame turning white or is it the flux residue? What kind of flux, WS or NC?
Electronics Forum | Thu May 17 07:43:24 EDT 2007 | d0min0
white residues but on top & bottom, flux is NC 94-rxzm from Cobar
Electronics Forum | Fri May 18 05:51:22 EDT 2007 | d0min0
I must improve rinsing for sure (no filtering of the water) but also a question - where do You buy/produce frames/carriers for both SnPb and LF wave processes we have just one supplier in France, we tried local ones but they lacked in precision...
Electronics Forum | Wed May 16 12:32:34 EDT 2007 | realchunks
Most Durastone product have a very low moisture absorbtion rate. This makes it ideal to water wash them. I wouldn't tlet them soak in the water, but you shoul dbe safe to wash them usinf water. Once the water is used up, you should treat it as a h
Electronics Forum | Mon May 14 10:05:12 EDT 2007 | d0min0
hi, i'd like to know how do you maintain cleaness of your solder frames after production - we use both SnPb and leadfree process, we clean in alcohol and ultrasonic but the frames look white and i wonder if we do not damage the structure??? best re