Electronics Forum | Wed Aug 27 11:25:11 EDT 2008 | blnorman
We use immersion tin boards and ENIG with Sn63Pb37 with no problems. We did have to tweak the profile higher with ImmSn though.
Electronics Forum | Wed Aug 27 07:13:05 EDT 2008 | eyalg
I need to solder SAC/HASL PC boards in a NON ROHS process (Tin Leaded solder paste and profile + Tin leaded components) Can I do that?? Regards, Eyal
Electronics Forum | Fri Aug 29 15:04:53 EDT 2008 | wavemasterlarry
Ha ha ha... I gotta admit it You sure are presistant with your companies wares.
Electronics Forum | Wed Aug 27 09:30:22 EDT 2008 | vladig
Hi Eyal, Sure you can do that. You might be able to use your "typical" reflow profile for eutectic, or tweak it slightly. it's a good idea to do a trial run and then get a couple of components cross-sectioned and checked for the microstructure of th
Electronics Forum | Tue Mar 20 06:42:32 EDT 2007 | Elena
I think, it will be no problems, if there's no Bi in a covering of components.
Electronics Forum | Sat Aug 02 06:40:51 EDT 2014 | madhuranatha
Will there be any issue if soder paste of SnPbAg is used for airborne application (PCB)
Electronics Forum | Tue Dec 30 21:14:22 EST 2003 | davef
You're thinking correctly. 80Au20Sn is incompatible with: * Sn/Pb * In/Sn * Sn/Pb/In * Sn/Pb/Bi Contact your solder supplier to obtain pictures of IMC.
Electronics Forum | Fri Apr 13 21:02:19 EDT 2007 | Sam
Anyone experience using SnPb wire to gold plated ICs? I have tried to solder the SnPb wire to the gold plated ICs lead, but the surface finishing is dull. Can anyone explain that to me? Why it is not shinny surface? Any recommendation?
Electronics Forum | Tue Mar 20 06:09:20 EDT 2007 | d0min0
Hi, can't find answer to my question on web - maybe someone can help would it be compatible to use a wire of Sn62Pb36Ag2 for a product made with Sn63Pb37 paste ??? regards
Electronics Forum | Thu May 06 10:52:08 EDT 2004 | John S
Many component manufacturers are moving to Pb free terminations. I've been doing a literature study of Pb free processing and have found several articles that indicate Pb-free paste with Sn/Pb terminations leads to early fatigue failures. Does anyo