Electronics Forum | Sat Aug 02 06:40:51 EDT 2014 | madhuranatha
Will there be any issue if soder paste of SnPbAg is used for airborne application (PCB)
Electronics Forum | Fri Oct 01 02:46:47 EDT 2021 | sn
Thanks, Evtimov. In terms of mechanical drop performance, can we conclude that the higher Ag alloy will have poorer drop shock performance relatively compare to those with lower Ag? The Ag3Sn is a good IMC for welding strength?
Electronics Forum | Fri Oct 01 01:25:55 EDT 2021 | sn
Thank you Djo for your sharing. By the way, do you know that which field/product will prefer to use SAC405 paste instead of SAC305 or lower Ag wt% alloy solder paste?
Electronics Forum | Mon Aug 04 15:46:05 EDT 2014 | dyoungquist
What do you mean by "airborne"? We have been using SnPbAg for 15+ years to build assemblies to IPC class II standards although with most assemblies going to Pb free, we are not using it near as much as we used to.
Electronics Forum | Tue Mar 20 06:09:20 EDT 2007 | d0min0
Hi, can't find answer to my question on web - maybe someone can help would it be compatible to use a wire of Sn62Pb36Ag2 for a product made with Sn63Pb37 paste ??? regards
Electronics Forum | Mon Aug 04 15:26:20 EDT 2014 | cyber_wolf
Whether or not SnPbAg will cause issues is trivial. You must build to the solder specified on the print.
Electronics Forum | Tue Mar 20 06:42:32 EDT 2007 | Elena
I think, it will be no problems, if there's no Bi in a covering of components.
Electronics Forum | Mon Aug 04 23:25:28 EDT 2014 | madhuranatha
Let me thank you for the reply. We are manufacturing products which are fitted on the aircraft. We are using SN63Pb37 solder paste for PCB assembly. Of late one of the solder paste supplier recommended SnPbAg for better solder-ability & reliabi
Electronics Forum | Mon Aug 04 23:27:05 EDT 2014 | madhuranatha
Let me thank you for the reply. We are manufacturing products which are fitted on the aircraft. We are using SN63Pb37 solder paste for PCB assembly. Of late one of the solder paste supplier recommended SnPbAg for better solder-ability & reliabi
Electronics Forum | Tue Nov 21 09:45:46 EST 2006 | russ
nope, but why such a high reflow temp for lead paste?