Hello Steve, Yes, there are differences in the various alloys and I have described briefly below these differences: SN100- a common name for 100% tin that is used to increase the tin content in 63/37. SN100C-Name for Tin/Copper/Nickel/Germanium all
Electronics Forum | Wed Nov 23 17:33:23 EST 2005 | adlsmt
Are the components 100% tin plated? Thats what we are buying and we have no problem at all soldering with the same profiles we always have used and we use the same alloy as you but different mfg. We have not had problems soldering tin plated parts wi
Electronics Forum | Tue Jun 07 16:19:58 EDT 2005 | davef
Q1) How to identify on good or bad ICs lead that could contribute to dewetting? A1) Distinguish between good or bad IC that could contribute to dewetting by testing for solderability, according to J-STD-002. Q2) What actions that must be taken in fa