Electronics Forum | Tue Jan 14 20:32:41 EST 2003 | davef
There's just about 4 beezillion companies that give solder training. Some are: * BEST Rolling Meadows, IL 847-797-9250 Bill Westmoreland (bwestmoreland@solder.net) http://www.solder.net/ * Circuit Technology 340 Raleigh St Holly Springs, NC 27540 (
Electronics Forum | Fri Jan 22 15:48:14 EST 1999 | Chrys
| Hello, | | I will be evaluating and qualifying two equipment types. The first is a fountain soldering device. I need practical advice on all the stuff you guys and gals know about as good, bad, ugly, best applications, setup, limitations, and all
Electronics Forum | Thu Jan 24 19:58:58 EST 2002 | davef
for regular eutecticish solders, keep the pot temperature between 230�C [446�F] and 290�C [554�F]. If you polled us on our pot temperatures, we�d be all over the map, but with more lower than higher than you. High pot temperatures tend to generate
Electronics Forum | Tue Sep 17 15:47:42 EDT 2002 | stepheno
Where I worked previously we had some boards with a couple 15 mil pitch parts. The first batch we got all had undersized pads. We had lots of bridging. We had less bridging with bigger pads. The ball size in the paste makes a bigger diffence regar
Electronics Forum | Fri Jul 13 09:27:15 EDT 2007 | losersk8er
Sorry I have just started working in this industry so I am not as familiar with everything. The probelm is with the Product shorting because of small pieces of metal stretching accross two leads of an IC. This could be a result of faulty equipment?
Electronics Forum | Mon Jan 17 17:38:29 EST 2011 | bandjwet
All: I am reaching out to get some suggestions on the right flux to use as well as a recommended cleaning process for soldering a KOVAR RF shield using 80/20 Au/Sn solder to a ceramic hybrid. The recommended profile is 4-5 min at 280C and at least
Electronics Forum | Mon Nov 20 21:02:46 EST 2000 | Michael Psrker
First question I have for you is: Are you assuming that standard precautions are in place at your facility to minimize moisture content i.e. air- deionizers, vacuum sealed packaging, humidity control in storage and manufacturing? You do not mention
Electronics Forum | Tue Feb 15 14:35:41 EST 2000 | Balas
hi I am designing a test vehicle with a range of components on it(pbga, cbga,fc, mbga, and qfps). My concern is that I would like to use a single stencil for solder deposition and not a stepped stencil. That would require me to have aperture design a
Electronics Forum | Fri Oct 01 14:16:15 EDT 1999 | Rick
I know there are a ton of variables that affect the overall height of a BGA after soldering to a PWB but... I'd like to know if anyone has done an analysis of (or if it's documented) as to what the pre and post reflow height dimension as measured fr
Electronics Forum | Sat Apr 24 08:23:03 EDT 1999 | Bubba
| Surprisingly enough, ever since the addition of an omega wave, we solder those often-troublesome SOT23's just fine and dandy.. anyways, long-term, well be getting a universal GDM which uses positive displacement pumps..currently we're using fuji g