Electronics Forum | Mon Dec 30 23:37:47 EST 2019 | agoesfirmanto
Hello All, I am a SMT Engineer from Indonesia, I am facing the problem of soldering balls in only one IC location, in other areas there are none. solder ball defect almost 30%. I have done several actions but failed to reduce the solder ball. 1.
Electronics Forum | Thu Aug 24 15:37:50 EDT 2006 | Chunks
Hi Any, This is from an earlies thread "Solder Ball After Reflow Process". Date: August 16, 2006 01:52 PM Author: Russ Subject: Solder Ball After Reflow Process Oven settings are meaningless here. What does the board see? It is the paste we a
Electronics Forum | Thu Dec 09 07:46:42 EST 2004 | davef
We did this for BGA pads, but have not thought about other types. So, this may or may not apply for those. Pad defined by:||Advantages||Disadvantages Non-solder mask||No point-of-stress concentration at edge mask and solder ball||Smaller pads have
Electronics Forum | Wed Dec 08 17:58:44 EST 1999 | Dave F
Dave: You should see a solder smudge on the gold plating where the ball was attached, if there is (was) solder reflow during either the (1) BGA fabrication, (2) your BGA attach, and / or (3) your BGA removal. You rework will not remove the solder
Electronics Forum | Tue Dec 07 20:07:21 EST 1999 | Dave C.
Thanks for all the info Dave. It's the interconnect between the copper foil pad and the eutectic solder ball that I'm most interested in. The BGA in question is very thin gold plated over nickel over the copper. When we are reworking the BGA, i
Electronics Forum | Wed Dec 08 10:10:41 EST 1999 | John Thorup
Hi Dave I think you just provided the key to understanding the problem. By your description you are talking about a CBGA (ceramic). These typically have balls composed of 10/90 Sn/Pb which melts at a higher temperature than the 62/36/2 Sn/Pb/Ag (or
Electronics Forum | Fri Dec 03 18:17:12 EST 1999 | Dave F
Dave: There's lots of stuff on the web describing BGAs. Examples are: http://www.smtnet.com/bookstore/publications/0speckdo1/s1.html http://www.smtnet.com/bookstore/publications/0shutcco1/ch1p2.html http://www.citizen-america.com/OEM/bga/process
Electronics Forum | Thu Mar 24 16:06:34 EDT 2011 | nkinar
Thanks for the reply, davef. Due to prototyping time constraints, I've been asked by the engineers if I could do something on the SMT line to salvage this prototype PCB. Could I do anything to connect the pad or fill the via? Much of the board h
Electronics Forum | Wed Apr 27 02:22:08 EDT 2005 | grantp
Hi, There are a number of things you can try. You are already using 1:1 hole to pad ratio, and that's good as you need the size. I would try an electroform stencil as that will have a smooth side of the aperture and help paste release. Don't use c
Electronics Forum | Tue Aug 04 14:29:14 EDT 2020 | dwl
Is the component an LGA or BGA? If its a BGA, it appears like the component is missing balls, if its an LGA, it appears like the solder isn't wetting to the component. What solder are you using? The wetting to the larger pads in the last pic seems
Main Products: 1. Original new and Original Used SMT/AI Spare Parts. 2. SMT Equipments And Related Machine( SMT Calibration, SMT Feeder Carts,Conveyer etc.) 3. Maintenace and Repair Service Pre-Sales Service Provide details ab
Manufacturer's Representative / Manufacturer / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
Building A, Jiepeng Square, Fuyong
Shenzhen, 30 China
Phone: 0755-33578694