Electronics Forum | Thu Aug 24 15:37:50 EDT 2006 | Chunks
Hi Any, This is from an earlies thread "Solder Ball After Reflow Process". Date: August 16, 2006 01:52 PM Author: Russ Subject: Solder Ball After Reflow Process Oven settings are meaningless here. What does the board see? It is the paste we a
Electronics Forum | Sat Feb 06 07:14:40 EST 2021 | agoesfirmanto
Dear Sirs, very sorry being late reply after a year. Thank you very much for your advices, you are absolutely correct after reduce grounding pad size. No more solder ball issue. Thank you very much. highly appreciate all of your supports. Best re
Electronics Forum | Mon Jul 07 13:33:40 EDT 2008 | realchunks
Most QFP 128s have a 0.16mm wide lead. Might have to modify your pads if you'r buying some odd ball part. But generally 0.2mm should be OK for this part. You may never get good toe wetting. Most QFPs are cut apart after plating, thus the toes are
Electronics Forum | Fri Jun 17 23:31:12 EDT 2005 | kenscj
Hi all, currently, we are seeing BGA problem like solder ball misalign, void, solder short (all under BGA, tested with 5DX), after reflow. We examine the solder ball (raw material of BGA), and see that the ball surface is not smooth, will that affe
Electronics Forum | Sat Jun 18 08:03:58 EDT 2005 | davef
kenscj: Responding to your points of interest: * On the smoothness of BGA solder balls causing solder ball misalign, void, solder short after reflow: We expect the solder balls to be smooth and have no sharp irregularities. We can't recall attribut
Electronics Forum | Tue Jun 21 11:46:04 EDT 2005 | kenscj
Hi dave, Thanks for the comment. I have another issue. The board already pass Test and Burn-In processes, but after 2 months the BGA contact is found open (no contact on certain balls). How can that happen? Is it during build, the solder ball alrea
Electronics Forum | Thu Jan 24 11:47:15 EST 2002 | Joe B.
Are there any formalized standards for the properties of solder balls? Example properties: sphericity uniformity(variance) of the ball size distribution surface roughness surface oxidation or other surface treatments/contaminants ?? As someone rela
Electronics Forum | Fri May 26 21:25:52 EDT 2006 | mika
Yes we do place "big and heavy" SMT DC/DC:s on most of our board's. Please tell us what brand it is or at least what the package look like?!? For instance we place a different numbers of "heavy" DC/DC converters (40x20mm & 45x25mm) that has the pick-
Electronics Forum | Wed Jun 09 17:53:06 EDT 1999 | Tom B.
| I am interested in seeing how some of you quote smt work. Currently we quote off a bom without component packages known then look in data books to find out what type of component they are. This job will be mine soon but i really believe there is a
Electronics Forum | Thu Oct 08 08:15:39 EDT 2009 | kpm135
We've used both 1A33 urethane and 1B31 acrylic coating on our SMT assemblies with great success for many many years. This is with components of all shapes and sizes including a 9 ball micro-BGA. We apply the coating in every way imaginable and we hav
Main Products: 1. Original new and Original Used SMT/AI Spare Parts. 2. SMT Equipments And Related Machine( SMT Calibration, SMT Feeder Carts,Conveyer etc.) 3. Maintenace and Repair Service Pre-Sales Service Provide details ab
Manufacturer's Representative / Manufacturer / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
3 Road Xintang， Fuhai Street，Fuyong
Shenzhen, 30 China
Phone: 13713862102