Electronics Forum | Mon Dec 20 07:58:02 EST 1999 | pascal MATHIEU
hello guys ; we are using a fine pitch component(0.65mm) on a thick copper PCB (Cu = 90�m) ; in this case we notice that we are in the process'limits , because the different supplier of the PCB are not able to ensure a good stability of it's process
Electronics Forum | Thu Sep 07 10:32:12 EDT 2006 | slthomas
Is the solder reflowing on the pad but not wicking up the lead, or does there appear to be insufficient solder to wet both, or is it not reflowing at all, or.....? Have you verified your profile? What is the condition of your paste (expiration date,
Electronics Forum | Wed Nov 06 19:03:33 EST 2002 | broncos
If you are certain that reflow process is good, I would suggest starting checking the following: 1. Check to see if leads / pads are contaminated or oxidized. However, this usually results poor solder quality throughout the board. 2. Check the amou
Electronics Forum | Thu Sep 07 07:41:06 EDT 2006 | Bubba
Check for coplaner leads if this just exists at reflow process, i.e. look at part before oven, turn on 3D at placement machine. If you see after wave solder, the wave could cause coplanarity issues on top as well if you are going slow enough to refl
Electronics Forum | Thu Sep 07 10:45:46 EDT 2006 | vicknesh28
Yes solder is reflowing on the pad but doesnt wick up the lead. Solder paste is sufficient. It just forms a saddle like appearance beneath the failing lead. The failed lead doesnt get reflowed at all. What puzzles me is how can hundreds of leads wet
Electronics Forum | Fri Sep 08 08:00:41 EDT 2006 | davef
That's your clue. Your reflow is running ~240*C and your soldering iron is running ~370*C. Dial-up the heat.
Electronics Forum | Thu Sep 07 03:47:07 EDT 2006 | vicknesh28
I have been getting non wets on fine pitch QFP packages on random leads during reflow process. I noticed that every time there is some flux residue left between the non-wet lead and the solder pad. No residue was not observed on the rest of the good
Electronics Forum | Wed Apr 11 14:05:30 EDT 2001 | davef
No, there's not a really great epoxy product for attaching thermocouples in reflow. Specifically, what's your problem? From Sanders Temprobe verbage ... Adhesives There are two general classes of material commonly used to adhesive bond thermoc
Electronics Forum | Wed Nov 06 16:31:59 EST 2002 | slthomas
I would also consider paste control (don't take it personally...I always have to get after people about this one), time on the stencil, time between print and reflow, solderability of the component leads, paste volume (that one really got us once....
Electronics Forum | Sat Oct 07 04:02:50 EDT 2000 | C.J. Long
Good morning, All: I am from PCB shop and one of our customer is experiencing solder bridge on 16 mil pitch QFP( immersion gold finish). Land width requirement is 8 +/- 1 mil measured over top of of land and our mean is 7 mil. Bottom land width is 8