Electronics Forum | Thu May 09 13:49:24 EDT 2013 | davef
First, it appears that your solder mask and your coating material appear to be incompatible. Second, IPA leaves a residue that's probably not compatible with your coating material, either. IPC-HDBK-830 - Guidelines for Design, Selection and Applic
Electronics Forum | Thu Jul 05 10:45:01 EDT 2001 | dougie
Steven, There is a load of info on this if you check through the archives. Quick pointer though are: Solder balls are caused by paste creeping under the component at placement. The part is placed and the paste is squashed under the component, when t
Electronics Forum | Tue Aug 10 07:28:49 EDT 1999 | Brian
| | | I am having cleaning problems when processing PCB's which have | | | TAIYO solder mask on them. After processing, hand soldering and | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide marks etc. Other
Electronics Forum | Tue Aug 10 15:19:55 EDT 1999 | Earl Moon
| | | | I am having cleaning problems when processing PCB's which have | | | | TAIYO solder mask on them. After processing, hand soldering and | | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide marks etc.
Electronics Forum | Tue Aug 10 15:47:34 EDT 1999 | John Thorup
| | | | | I am having cleaning problems when processing PCB's which have | | | | | TAIYO solder mask on them. After processing, hand soldering and | | | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide mark
Electronics Forum | Tue Aug 10 16:01:12 EDT 1999 | Earl Moon
| | | | | | I am having cleaning problems when processing PCB's which have | | | | | | TAIYO solder mask on them. After processing, hand soldering and | | | | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tid
Electronics Forum | Tue Nov 21 09:46:19 EST 2006 | jax
I assume you are talking about Sn62Pb36Ag2 solder. You should not see any added concerns when subjecting Sn62 to multiple reflow cycles as compared to Sn63. As compared to Sn63Pb37: Reduced leaching issues Increased Wetting due to lo
Electronics Forum | Fri Dec 18 09:07:24 EST 2009 | tommyg_fla
dave, where I work they are having the same problems with 1B31 acrylic. The coating thickness is 6-8 mils dried so that have to do several passes with an air dry between them and a final oven cure. They think that it might be related to the heating r
Electronics Forum | Tue Sep 08 14:35:12 EDT 2009 | davef
Maybe your solder mask supplier can provide additional background
Electronics Forum | Thu Sep 03 14:21:29 EDT 2009 | davef
Creeping corrosion occurs on bare metal. Most commonly, it is seen on boards with thin protective coatings [eg, bare copper, immersion silver, organic solderability preservative]. Look here: * enthone.com/docs/AlphaSTARCreeping.pdf * circuitree.com