Electronics Forum | Wed Mar 01 10:46:26 EST 2000 | Robert Hartmann
Kelvin, Thanks for the help. The actual opening size is .440 mm, but I think what you said makes sense. After discussing with the customer, it looks like it is the height which matters, more than the diameter. We have learned that the height of t
Electronics Forum | Fri Jan 15 08:11:34 EST 1999 | Jim Nunns
Our spec on voids is 30% ball diameter in the center. On the component to ball and pad to ball interface, we use 25%. To determine this spec, we asked around. I don't know of any studies that have been done to verify if this is OK Regards Jim |
Electronics Forum | Fri Jan 15 15:29:03 EST 1999 | Jason Hall
| Our spec on voids is 30% ball diameter in the center. On the component to ball and pad to ball interface, we use 25%. To determine this spec, we asked around. I don't know of any studies that have been done to verify if this is OK | | Regards | Ji
Electronics Forum | Sat Jan 16 03:06:36 EST 1999 | Wirat S.
| | Our spec on voids is 30% ball diameter in the center. On the component to ball and pad to ball interface, we use 25%. To determine this spec, we asked around. I don't know of any studies that have been done to verify if this is OK | | | | Regard
Electronics Forum | Fri May 26 16:24:45 EDT 2006 | Jak
Due to spacing issue, we are considering using power bricks with tin/lead solder ball instead of PTH package. The solder ball is 40 mil diameter. Our CM suggested they do hand place since the pick and place nozzle cannot pick up and hold the part due
Electronics Forum | Wed Feb 01 11:33:37 EST 2017 | emeto
Joshua, 100um is 4mil aperture. You should ask several stencil houses about the possibility to print that small amount of paste(type 6 paste is available now with very small solder spheres 5-15um diameter). Even applying small amount(thin layer of f
Electronics Forum | Thu Apr 05 22:27:06 EDT 2001 | davef
As a band-aid, consider running your chip wave when soldering these boards [Similar to Cals "dance with me babe" suggestion.] If the problem is as broad based as you say and the radial components have a tight fit, consider increasing the holes by a
Electronics Forum | Fri May 07 05:47:44 EDT 1999 | Charles Stringer
This is not strictly a surface mount query but any input welcome I am thinking of using surface mount solder thief pads for a through hole connector. The connector is two rows of 0.1" pitch pins and on waving there is often a bridge on the last two p
Electronics Forum | Mon May 15 10:16:36 EDT 2006 | slaine
Hi Im trying to find a supplier for 30swg HMP solder wire idealy the alloy I want is 93.5Pb, 5Sn, 1.5Ag, 296 to 301 degrees C. Flux cored. 30swg or 0.3mm diamiter. but the critcal parts are the diameter and the melting point, 300 degrees +-20 degree
Electronics Forum | Mon May 14 12:44:08 EDT 2012 | tomgervascio
I am a user of an Ersa Versaflow 3/45. I was wondering if anyone could share some process pointers. I have a 0.125" multilayer PCB that I am having problems consistently achieving 75 percent hole fill on a mini-coax connector. The coax connector ha