Electronics Forum | Mon Oct 11 06:00:27 EDT 1999 | Brian
| Folk's, | | I'm just tying up some loose end's on my Master's Thesis on solderballing @ wave soldering and the effect the topography of the mask / PCB has on it. | I was wanting to do a straw poll on you guy's as to the type of resist's you are us
Electronics Forum | Wed Apr 21 20:50:26 EDT 1999 | Dave F
| I'm having problems with trying to get a good solder joint using a Ceramic PCB. We are using AMTECH hi-temp solder (ws-486 96.5/3.5ag). My profile looks great and I used the recommended profile from Amtech with a few adjustments. My max temp is abo
Electronics Forum | Mon Dec 22 19:43:43 EST 2003 | Dean
I have seen this affect on Immersion Tin and OSP. 70 to 90 % of the solder wicks to the lead and forms a "single" homogenous solder mass. This even though the pad was 100 % covered with paste... Evaluated different solder paste...did find variatio
Electronics Forum | Tue Sep 14 08:46:31 EDT 2004 | scombs
I'm currently working for a OEM that has 700+ stencils in house and we received 30 to 40 stencil a month. We recently switched to a no clean process which is causing the stencil part numbers to disappear from the stencil frames due to the saponifier
Electronics Forum | Mon Mar 27 21:09:29 EST 2006 | ms
Thanks Dave I'm not convinced the air is necessarily in the paste from manufacture - suspicious that it may be folding in during the change in direction of the print cycle - or as the paste travels across apertures. It is not necessarily in the fir
Electronics Forum | Fri Jul 21 11:30:39 EDT 2000 | Joe H.
Craig, Since you didn't share any detail regarding the component side of the board or what other components reside on the bottom side, I'm prepared to take a stab in the dark. Have you considered doing a double sided reflow on this board? Also
Electronics Forum | Tue Sep 20 17:15:29 EDT 2005 | valuems
Hello I'll be the one to ask a dumb question--Why not fix the screen printer? If it is a MPM you can call me and I'll help if I can. And no I'm not trying to sell any thing. Better yet --why is the printer down? Wasn't thinking that you may be ou
Electronics Forum | Thu Jun 01 16:30:05 EDT 2006 | slthomas
Just wondering if anyone knows this off the top of there head. I might be able to figure out the math based on surface tension (this is 63/37 so the data is out there) but I REALLY do not want to put that kind of effort into this. :/ Editing to clar
Electronics Forum | Wed Apr 21 22:15:12 EDT 1999 | Chris
| I'm having problems with trying to get a good solder joint using a Ceramic PCB. We are using AMTECH hi-temp solder (ws-486 96.5/3.5ag). My profile looks great and I used the recommended profile from Amtech with a few adjustments. My max temp is abo
Electronics Forum | Fri Jan 15 09:27:18 EST 1999 | Earl Moon
| I saw the problem of void in solder bump or in lead less component or some BGA. But I didn't have standard specification of that void is accept or reject? Do any body have the better idea or suggestion of the criteria ? | | Thank you, | Wirat