Electronics Forum | Wed Jul 03 03:02:35 EDT 2013 | autoel
How to test the reflow solder joint shear strength? What are the specification to test solder joint shear strength? What are the different methods to test the solder joint shear strength? Vijayashree
Electronics Forum | Mon Feb 02 12:36:41 EST 2004 | paul_bmc
90% of the assemblies our company produces are class 3 and we have no problem at all inspecting or getting class 3 quality through reflow. Rarely do we have touch up because of insufficient or poorly reflowed solder joints. What are the problems you
Electronics Forum | Wed Jan 28 14:35:12 EST 2004 | swagner
Has anyone in the industry had even a fair amount of success inspecting reflowed solder joints to IPC class 3 standards? I am not interested in hearing from system reps or people who work for an AOI manufacturer. Thanks,
Electronics Forum | Mon Feb 02 17:52:11 EST 2004 | swagner
We are not having a problem, we have a customer that would like us to use post reflow AOI to inspect the solder joints to class three. I would like to see if anyone is having sucess doing this.
Electronics Forum | Tue Feb 03 12:39:20 EST 2004 | paul_bmc
We had the data at the time and it was quite high. More false calls then anything. I do not have the data anymore it since has been archived. When the system was introduced we had 1 engineer and 2 operators trained for programming and running the
Electronics Forum | Tue Feb 03 12:24:56 EST 2004 | swagner
Paul, do you have any kind of false failure data for the application you struggled with? Also what amount of manpower did you use to operate the system(s).
Electronics Forum | Tue Feb 03 06:52:45 EST 2004 | paul_bmc
About 2 years ago our company tried to go with a post reflow AOI inspection. This AOI was suppose to be able to inspect to a level class 3 product. **It is impossible** You cannot inspect for a heel fillet and inspecting for poor wetting is a very
Electronics Forum | Wed Jul 03 15:40:17 EDT 2013 | davef
Shear tests are [in my opinion] senseless. The shear stress you measure depends more on the shear rate and on the point where the force is applied than on the grain structure. When shearing a component, you not only apply shear stress, but also roll
Electronics Forum | Mon Feb 02 22:01:24 EST 2004 | Dean
I find this disturbing when customers dictate your process and equipment? Your responsibility is to deliver a quality product on time. Why would your customer care HOW you achieve this? Hence the success of Chinese manufacturing. I have one custo
Electronics Forum | Mon Jun 12 06:45:10 EDT 2000 | kim ji tae
Hi! Thanks all who upgrade these pages. I have some questions. Is there any answer? I do double-sided reflow solderig, with 0.4% AG solder cream. with AU finished pcb. First I do reflow solder bottom side where 0.5pitch TQFP locates. Second I do re