Electronics Forum | Tue Sep 10 07:24:13 EDT 2002 | John
I need teoretical info for theme "Matted surface vs solder ball". Is it right that some solder pastes decrease solder balling but give matted surface after reflow? That diference between these pastes and others? Are the matted surface worse solder b
Electronics Forum | Tue Feb 03 06:52:45 EST 2004 | paul_bmc
About 2 years ago our company tried to go with a post reflow AOI inspection. This AOI was suppose to be able to inspect to a level class 3 product. **It is impossible** You cannot inspect for a heel fillet and inspecting for poor wetting is a very
Electronics Forum | Tue Feb 03 12:39:20 EST 2004 | paul_bmc
We had the data at the time and it was quite high. More false calls then anything. I do not have the data anymore it since has been archived. When the system was introduced we had 1 engineer and 2 operators trained for programming and running the
Electronics Forum | Wed Jul 03 15:40:17 EDT 2013 | davef
Shear tests are [in my opinion] senseless. The shear stress you measure depends more on the shear rate and on the point where the force is applied than on the grain structure. When shearing a component, you not only apply shear stress, but also roll
Electronics Forum | Mon Feb 02 22:01:24 EST 2004 | Dean
I find this disturbing when customers dictate your process and equipment? Your responsibility is to deliver a quality product on time. Why would your customer care HOW you achieve this? Hence the success of Chinese manufacturing. I have one custo
Electronics Forum | Mon Apr 17 19:30:27 EDT 2000 | Boca
All of the above is good stuff. To add, I have seen this several times if the assembly is wavesoldered. Heat from the wave can partially reflow the top side SM solder joints and weaken them. To test, check joint strength before wave and then after
Electronics Forum | Fri Jun 02 16:30:42 EDT 2000 | Michael Parker
I found a reference to Cost of Conversion earlier this year. Basically, the average cost to convert a single component from raw materials to assembled goods is $.08, just after pick and place. After placement and before reflow, repair (solder paste r
Electronics Forum | Fri Aug 10 13:09:49 EDT 2001 | Hussman
Hey Wister, Assuming you are talking about BGA voids, and you just want to try and optimize your profile, you could try a "straight ramp profie". This is where the soak temp is constantly being elivated until you hit reflow. I find this helped me
Electronics Forum | Mon Oct 18 11:01:26 EDT 2004 | DenisM
I have had similar problems and my customers have had this too. A two story drop test was made by one of my customers and they found that changing Sn63 solder to Sn62 solder made a significant impact. There is no real downside other than a slightly
Electronics Forum | Thu Mar 24 19:17:43 EST 2005 | EA
Hi, We are running the automotive product and question was throw to us how do we ensure that our solder joint are good enough after reflow.....and during the sealant process, there's a bit of bend on the nozzle and it toughes the component and custo
.jpg)