Electronics Forum | Sun Aug 15 05:45:15 EDT 1999 | Brian
Boca, Dave Sorry, but I cannot let this go. I'll go along with you that, at the time that the Montreal Protocol was initially signed (September 1987), there was no scientific proof that CFCs etc. were causing ozone depletion. There was, however, ve
Electronics Forum | Thu Aug 12 22:23:23 EDT 1999 | Dave F
| | | | (snip) | | | | | | You're quite right. However, anyone who uses MeCl in an aerosol spray needs his head examining. I'll go further: if he continues, he will most CERTAINLY need his head, the rest of his CNS and his liver examining a little
Electronics Forum | Fri Aug 13 10:39:25 EDT 1999 | Boca
| | | | | | (snip) | | | | | | | | You're quite right. However, anyone who uses MeCl in an aerosol spray needs his head examining. I'll go further: if he continues, he will most CERTAINLY need his head, the rest of his CNS and his liver examining a
Electronics Forum | Thu Oct 14 23:19:25 EDT 1999 | Dennis O'Donnell
Water soluble masks are great in my book. After having used the latex type, I found that the water soluble will save a lot of time. I dont't use a closed loop system, but I do have a filter on my discharge line. I have not experienced any filter c
Electronics Forum | Mon Apr 17 19:44:20 EDT 2000 | Dave F
Ashok: Well, your customer probably has a good reason for wanting you to send them boards without holes in the solder mask. What is their goal for the mask capabilities after you get do reworking the boards? * Cosmetic surface coat? * Performance t
Electronics Forum | Fri Apr 14 19:09:38 EDT 2000 | Ashok Dhawan
One of our customer insist on repair of solder mask even if it is pin holes or less than 0.010 sq in. area. Based on our knowledge bank, we though of thre options, there could be many more. 1. coat the exposed area with original solder resist (from
Electronics Forum | Mon Nov 08 12:47:52 EST 2004 | clampron
Good Day Everyone, I have a BGA rework that has some chipped/damaged solder mask that will need to be repaired prior to BGA replacement. I was wondering what materials are being used in the industry for this type of application. Any help would be g
Electronics Forum | Tue Nov 09 10:44:13 EST 2004 | russ
I guess i might want to throw this in for future reference. After speaking with our board supplier he states that this mask is fully cured when it reaches approximately 180C. I beleive this since we usually probe the repaired area after putting the
Electronics Forum | Sun Jan 31 23:03:57 EST 1999 | Dennis O.
| | hi, | | i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier pr
Electronics Forum | Tue Nov 24 05:23:18 EST 2009 | prodivegsr
Hi Davef, Thanks...Saw 1 of your thread that you posted : Thanks for providing... From davef : There are many possibilities: * Conformal coat is incompatible with surface residue on the board * Conformal coat is incompatible with solder mask on the