Electronics Forum | Tue Dec 17 16:27:02 EST 2002 | davef
I�m not clear on the problem. What I get: * Your fabricator did not deliver the product that you asked for in your purchase order. * Pad. Land. A portion of a conductive pattern used as a termination area. Metal surrounding a hole on a printed ci
Electronics Forum | Tue Aug 10 07:28:49 EDT 1999 | Brian
| | | I am having cleaning problems when processing PCB's which have | | | TAIYO solder mask on them. After processing, hand soldering and | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide marks etc. Other
Electronics Forum | Tue Aug 10 15:19:55 EDT 1999 | Earl Moon
| | | | I am having cleaning problems when processing PCB's which have | | | | TAIYO solder mask on them. After processing, hand soldering and | | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide marks etc.
Electronics Forum | Tue Aug 10 15:47:34 EDT 1999 | John Thorup
| | | | | I am having cleaning problems when processing PCB's which have | | | | | TAIYO solder mask on them. After processing, hand soldering and | | | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide mark
Electronics Forum | Tue Aug 10 16:01:12 EDT 1999 | Earl Moon
| | | | | | I am having cleaning problems when processing PCB's which have | | | | | | TAIYO solder mask on them. After processing, hand soldering and | | | | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tid
Electronics Forum | Wed Oct 13 14:27:08 EDT 1999 | mikeh
Dave F, We are currently using a latex based ambient/thermal cure material that is applied by hand or automated dispensing equipment. Printing is an option for us, but we have not had much luck with this particular material. The mask is peeled off a
Electronics Forum | Tue Feb 09 16:53:06 EST 2021 | SMTA-64387083
The size of the pad changes among the two. A solder mask defined pad will always be larger than a copper defined by your mask expansion setting. This will affect paste volume, if your standard paste aperture is designed for copper defined pads you m
Electronics Forum | Tue Feb 01 21:53:06 EST 2000 | Dave F
Emmanuel: You have choices to prevent the solder paste from flowing to the second side during reflow: 1 Have your board fabricator plug the vias. 2 Put a temporary solder mask on the secondary side vias. 3 Have your designer relay-out the vias unde
Electronics Forum | Fri Jun 16 10:38:33 EDT 2000 | Iain
I have 15 very large backplanes (.156" thick Au plating) that the ground pins of a high density thru-hole connector were not thermal relieved in the artwork. As a result we are unable to solder the 8 pins that connect to the ground plane. We know t
Electronics Forum | Mon Aug 21 19:38:33 EDT 2000 | Dave F
Eric: I�ll pass on the uV and ammonia, also. Thoughts are: 1 You�re correct that the temperature/humidity mix can be a big driver to latex peelable solder mask cure time, but don�t overlook material thickness. Dispensers put material in a very th