Russ, The caps are 0603 case size. I am not sure about the manufacturing details, as I work for the capacitor supplier. The manufacturing details are unclear at the moment, as the customer (South of the border) has not released such detailed inform
Electronics Forum | Thu Jul 03 07:43:50 EDT 2003 | davef
So, there is a crack or gap between: * Solder and component termination. * Component termination and component body. Correct? Describe: * Coarseness / smoothness of the metal on the termination underneither the crack. * Solder left on the terminatio
Electronics Forum | Thu Aug 10 03:30:42 EDT 2000 | JohnW
Ramon, Solder ball' are a bitch aint they?, identifying the right location to fix em is a bigger one. As you and the rest of teh guy's have said yes you'll need to look at your stenil..but maybe your stencil is good so you'll need to look else where
Electronics Forum | Fri Dec 17 08:05:00 EST 2004 | davef
Your solder paste is talking to you, follow its message. Listen to the paste. Be at one with the paste. If you insist on ignoring the message of the paste, add more paste, if you just need to complete the last board or so, but you really should ju
Electronics Forum | Sat Jun 02 16:20:06 EDT 2012 | davef
While the only way this thread could look more like a stealth advert is if it has the word 'advertisement' blinking at us, I'll play along. Questions are: * Have you asked the supplier Fantron Technologies [sales@fantron.com] what they suggest? * Wh
Electronics Forum | Fri Sep 21 14:03:45 EDT 2001 | jschake
I have observed solder balling for all aperture sizes tested. Solder balling levels appear to be better correlated against the amount of solder paste that is underneath the 0201 component terminations after placement rather than comparing this to th
Electronics Forum | Wed Aug 30 16:00:42 EDT 2000 | Dave F
Russells: You can mix the two solders you mentioned, assuming by "96s" you meant "96Sn / 4Pb". If you heat the two tin / lead alloys to a liquid state, you�ll form a tin / lead solution with properties different from either of the two solders. The
Electronics Forum | Wed Jun 30 10:37:11 EDT 1999 | Boca
We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design). Inste
Electronics Forum | Mon Jun 12 22:02:48 EDT 2000 | Dave F
Jason: Wave soldering is the coolest thing!!!! First, so, what�s the chemical analysis of this white res? Can you point us to either tin, rosin, or something else? Second, how do you know that you are making these white residues? Could your boar
Electronics Forum | Fri Apr 22 16:57:10 EDT 2005 | davef
Suppliers are: * Contax Ltd Little Park Farm Road Segensworth West Fareham, Hants, PO15 5SJ UK +44 1489 885808 Fax: +44 1489 885553 * Leister Process Technologies Riedstrasse Sarnen LCRN, 6060 Switzerland 011-41-416627467 Fax: 011-41-416627480 * mt