Electronics Forum | Sat Jan 12 11:47:25 EST 2019 | ranap121212
I am looking for a good material for selective nozzle. We are currently using Kovar but it is expensive and wears out it has very good wetting properties.I looking for a material or coating that would allow me to keep the binder flow and with less co
Electronics Forum | Fri Dec 10 01:02:36 EST 2010 | sparrow
Hello, our products are made on single-sided boards and we often have problems with receiving too warped PCBs from our suppliers. Can anybody suggest a good laminate or the most important properties of the material so we could specify it when we orde
Electronics Forum | Fri Dec 29 16:38:15 EST 2017 | mekmat544
Hello all, I would like to ask you about difference between wettable and nonwettable solder nozzle: Are there some pros and cons for each type? Thank you. Mekmat
Electronics Forum | Tue Jan 25 09:04:02 EST 2005 | Indy
Are you soldering to polymide material or nickel tin ?
Electronics Forum | Mon Jan 24 20:59:34 EST 2005 | davef
What is your specific problem when soldering polyimide [amide]?
Electronics Forum | Fri Jan 21 13:29:35 EST 2005 | vinod
Hi Friends, I had a PCB with polymide material with nickle tin plating on it. I had real hard time to do hand solder. I am asking help if any one have any experience with polymide material.
Electronics Forum | Sat Jun 23 09:56:04 EDT 2007 | slthomas
Every plant I've worked at used copper. I don't know your criteria for better, but I would think soldering and hanging copper would be a lot easier/quicker than threading and hanging iron. I haven't priced either one, though.
Electronics Forum | Sat Jun 23 11:35:58 EDT 2007 | grantp
Hi, Yes, we just built a new plant, and used copper again. The stuff we cut out of the old building was copper, and it was fine without any issues. We lay it on an angle so condensation flows to an end, and can be periodically vented, and we take a
Electronics Forum | Tue May 04 10:30:35 EDT 1999 | Dave F
| I am about to embark on an effort to evaluate 3 different solder material suppliers and their recommended materials for our assembly process, in an effort to find the best supplier/material. We do mixed technology, with NOCLEAN chemistry so I will
Electronics Forum | Mon May 03 17:23:24 EDT 1999 | Kelly Morris
I am about to embark on an effort to evaluate 3 different solder material suppliers and their recommended materials for our assembly process, in an effort to find the best supplier/material. We do mixed technology, with NOCLEAN chemistry so I will b