Electronics Forum | Wed Jun 16 07:01:26 EDT 2021 | tommy_magyar
Hi Edgar, I am not aware of any standards either, but from own experience can tell that if there are boards going through oven with PPM between 1500-2000 the solder will be dark (unaesthetic) although some of our customers accepted them if they were
Electronics Forum | Thu Jun 10 13:29:21 EDT 2021 | edgar_smt_ap
Good morning. What should be the Oxygen content Standard in an Oven? Here in my company, we have an ERSA reflow Oven, and we work with Lead Free solder paste. According to Work Standard documents send by my company corporate, the PPM Oxygen conte
Electronics Forum | Tue May 04 14:45:40 EDT 2010 | bruna
Hello Does anyone can give feedback about this two analyzers (zirox and delta f 150)? In fact we are trying to understand which is better for wave soldering, benefits and prejudice. Does anyone work with both? Thanks
Electronics Forum | Tue Aug 25 11:31:41 EDT 2020 | stephendo
yes Once I was using dewers of liquid N2 and recommended switching. I tried using air to the machine so the sensor would let the machine run. Boards went from good to a two inch icicle covering a large area. We went to a wall mounted single stage fi
Electronics Forum | Wed Jun 14 08:08:56 EDT 2000 | Wolfgang Busko
Hi ji tae, we had a similar problem with QFPs 0,5 pitch processed by one subcontractor. The symptoms we noticed were: - the solderjointshape and wetting looked normal - the surface had a dull gray appearance - by pushing a lead sideways with a tweez
Electronics Forum | Mon Aug 16 05:42:53 EDT 1999 | Omat Marasigan
Hello reflow experts, I just wanted to know the effects of N2 and O2 on reflow furnace to the solder ball apperances. thanks in advance.... ...Omat
Electronics Forum | Mon Aug 16 09:50:20 EDT 1999 | Earl Moon
| Hello reflow experts, | | I just wanted to know the effects of N2 and O2 on reflow furnace to the solder ball apperances. | | thanks in advance.... | | ...Omat | | Not really that much with eutectic balls and solder pasted pads and the reflow
Electronics Forum | Tue Jul 06 14:23:27 EDT 1999 | Earl Moon
| | | I've heard that use of VOC free flux with wavesolder fixtures can be challenging due to entrapment of water in the fixture. | | | | | | Is anyone out there successfully running VOC free with wave fixtures & did you experience problems? If so,
Electronics Forum | Mon Dec 11 14:30:46 EST 2023 | proy
We all know that purity of nitrogen is critical for selective soldering. When it comes to wave solder- how much or what percentage reduction in oxygen is enough to make a difference in 1) at least reducing dross buildup and 2) being anble to cut ba
Electronics Forum | Mon Oct 01 15:44:13 EDT 2007 | hussman
A simple answer is never. Tin lead will oxidize when exposed to oxygen, but it will not rust away like normal steel. I have old equipment from the 1920�s and 1930� that have solder joints as robust as the day they were made. Maybe not as shinny, b