Electronics Forum | Tue Jun 09 07:10:46 EDT 2020 | ameenullakhan
Hi Team, Please recommend some good solder paste viscosity meter.Which easy to use and user friendly. Regards, Ameen
Electronics Forum | Mon Jun 22 16:33:59 EDT 2020 | davef
Measuring solder static paste viscosity is fairly easy to do. IPC TM-650 .4.34, Solder Paste Viscosity lists the method and equipment. Just don't tell your customer that it is meaningless because the solder paste is printed in shear, not statically
Electronics Forum | Fri Jun 19 22:10:18 EDT 2020 | davef
Don't get yourself wrapped around the measure solder paste viscosity axel. Observe the paste handling and preparation instructions provided by your solder paste fabricator.
Electronics Forum | Mon Jun 22 15:53:35 EDT 2020 | cyber_wolf
This would be a highly unusual "requirement." In house checks on paste viscosity went the way of the buffalo years ago. The question to your customer should be: why ? All of the mainstream paste suppliers should be able to supply you with a COC th
Electronics Forum | Mon Jun 22 05:04:57 EDT 2020 | ameenullakhan
Hi Dave, Thanks . But it's one of our customer requirement to have in house solder paste viscosity measurement. Regards, Ameen
Electronics Forum | Tue Jun 23 05:48:17 EDT 2020 | ameenullakhan
Hi Sr Tech, Yes we do have a COC for every solder paste with viscosity measured. But some customers have there unique requirements. And its not useful arguing with them. Regards, Ameen
Electronics Forum | Tue Jun 12 13:53:43 EDT 2001 | Eliud Rivera
We are trying to quilify a No-Cclean solder paste and we would like to know what kind of criterias or measurments are use to qualify the amount residues? Can we use an omega meter for that? What equipment measures SIR?
Electronics Forum | Sat Mar 30 13:33:50 EDT 2019 | stephendo
This is not an HVAC unit. This is a small unit attached to a production machine to keep the solder paste from drying out prematurely or slumping. The volume of air being cooled and desicated would be less than 3 or 4 cubic meters.
Electronics Forum | Tue Jun 23 05:52:15 EDT 2020 | ameenullakhan
Hi dave, Thanks for the input. your valuable feedback always help. which method is better Spindle or T-bar. IPC TM 650 have are considered as standard methods. 1. T bar 2. Spindle. since we have never used it. we are bit confused. Which would be
Electronics Forum | Wed Oct 07 06:22:23 EDT 1998 | Charles Stringer
| I am trying to find out, what possibilities I have, to print solder paste on a board, when the task is to have 120 Microns thickness for the biggest part of the board (85% of the real estate), and then have 250 Microns of thickness on the remainin