Electronics Forum | Tue Nov 28 15:10:50 EST 2006 | M. Sanders
Unfortunately, I don't have a copy of IPC-A-610 D on hand, however, I believe in IPC-610, this �floating height� between lead and pad has no maximum specification restriction. As long as there is no voiding, it is still acceptable for all 3 classes.
Electronics Forum | Fri Sep 24 09:49:53 EDT 1999 | C.K.
Hi Folks: We've been having bridging problems on our fine-pitch QFP's, despite thorough inspection of paste height, volume, and placement accuracies....profiles look good also. The bridging is happening after coming out of reflow...one last thing t
Electronics Forum | Tue Sep 24 11:10:07 EDT 2002 | Gregg Temkin
I�d appreciate assistance in trying to resolve a placement/soldering problem. My company has designed a board which uses a large number of 0402 LED�s that are .028� high. The LED�s need to be soldered so that they point straight up and are not til
Electronics Forum | Tue Sep 24 22:29:04 EDT 2002 | davef
First, I don't have a clear fix on the problem. Please drill-down to more detail. We appreciate that you probably don't know the parlance. Just describe what you have and then what you'd like to have. Second, most 0402 LED are fabricated just lik
Electronics Forum | Mon Apr 07 11:39:55 EDT 2003 | russ
How thick is your stencil? We print 16mil every day with type 3 paste 2 of which you have tried (Alpha and Kester) Stencil should be 5 mil. Russ
Electronics Forum | Wed Sep 07 03:03:35 EDT 2005 | Milroy
I am engaged with SMT production and we are going to have a brand new SMT line and I am studing about the screen printing and I have seen most commonly used stencil thickness is 6mil and I need to know what is the best solder paste height we can achi
Electronics Forum | Mon Apr 07 13:02:30 EDT 2003 | kmorris
Sorry, I forgot to include the stencil thickness. It is 5 mil. Thanks for the input, everbody. I just checked with our stencil supplier & I thought that Electro-polish was standard with lazer, but I now find out it is not. Our stencil did not get
Electronics Forum | Mon May 06 11:45:32 EDT 2019 | slthomas
There are quite a few papers out there on the subject. Just enter "SMT void reduction" into google or other search engine and take your pick. That said, slow ramp rates and paste volume reduction are a good place to start. Although I haven't tried i
Electronics Forum | Mon Apr 07 12:21:02 EDT 2003 | davef
Russ is correct. A 5 thou thick stencil should give good release. Here's how you run through it: * You want at least 5 solder particles across the smallest aperture. So in your case, 8 thou wide, which equals to 0.20mm gives us 0.20/5=40 microns.
Electronics Forum | Sat Mar 11 11:57:37 EST 2017 | parto
Dear experts, I'm looking for answers of my following questions: 1. What average consumption of soldering paste in SMD per square meter? 2. What average consumption of soldering bar in THD per square meter? Thanks in advance. Best regards, Reza