Electronics Forum | Thu Apr 26 09:03:35 EDT 2007 | ck_the_flip
3d is good for initial verification that your screen printer and stencil is producing the desired paste height. 2D verification is more than sufficient during regular production. That being said, your best bet for a 3D machine is to go cheap - buy
Electronics Forum | Thu Apr 26 19:06:08 EDT 2007 | grayman
In short this guys are not well updated on the new technology of SPI. True, 3D IN LINE SPI is no longer a slow machine. Try checking some brand like Cyberoptics,Synapse imaging,SEIMENS,KOHYOUNG and many others...they can match the speed os some mount
Electronics Forum | Fri Apr 27 10:33:58 EDT 2007 | ck_the_flip
Jeremy, well said! Thanks for "validating" my theory... LOL I agree that the sampling frequency, AND methodology are key things with 3D inspection. 3D will give you some insight onto how your paste (rheology, viscosity, thixotropy)AND process are
Electronics Forum | Thu Mar 22 17:38:44 EST 2001 | davef
OK, lemme take a different angle on this, �cuz I forgot to touch on this when I first responded. I mentioned a study ["Evaluation of Low Residue Soldering for Military and Commercial Applications: A Report from the Low-Residue Soldering Task Force"
Electronics Forum | Tue Sep 22 10:29:18 EDT 2009 | stepheniii
To how many decimal places? Do you want to have a factor for different screen printer operators? There is no such formula and I doubt there ever will be one with any real accuracy. The stencil house might be able to tell you the total area of the
Electronics Forum | Fri Jan 24 08:14:24 EST 2014 | davem
m_imtiaz, Over the last 15 years or so I've found that using the stencil foil thickness +2mils/-0mils has worked very well. For example, if you have a 5mil stencil thickness your upper control limit would be 7mils and your lower control limit would
Electronics Forum | Thu Mar 22 16:35:06 EST 2001 | Steve
Deja vu! When I read your response I turned around to see if you standing behind me listening to our problem. We currently make about 50 different boards all using no-clean that have no problems, yet this newest boards has a couple of issues that eng
Electronics Forum | Fri Aug 18 05:43:51 EDT 2000 | Richard Berry
Thanks Wolfgang / Charles Have tried method suggested by Wolfgang on one product, and seem to be a bit over (perhaps density calculation was a bit out). Also, the volume of paste deposited must be less than the voume of the apetures on the stencil b
Electronics Forum | Sat Nov 08 07:05:12 EST 2008 | davef
Often, your solder paste supplier provides guideline on handling their solder paste. For instance: http://www.aimsolder.com/techarticles/tech%20sheet%20paste%20handling.pdf We have no relationship, nor receive benefit from the company referenced ab
Electronics Forum | Mon Mar 05 11:04:14 EST 2007 | Yngwie
We are exploring ways to reduce the waste of solder paste. Here are some of the ideas I have in mind: 1) To use paste supplied in Syringe instead of jar. Paste that are opened more than 8 hours will normally be discarded, so we are looking for ways