Electronics Forum | Thu Jan 14 09:25:34 EST 2016 | davef
IPC-A-610F 10.2.6 Laminate Conditions - Depanelization talks to the acceptability of the depanelization criteria for assembled boards. There is no requirement for moisture sealing with epoxy or other material. Basically, the standard requires that th
Electronics Forum | Wed Jul 27 09:58:05 EDT 2011 | davef
Pressure printing systems Conventional stencil printing techniques have fundamental limitations as regards paste handling: The volume of paste available for printing is limited, so frequent replenishment is necessary Paste is difficult to c
Electronics Forum | Thu Dec 10 09:06:47 EST 2009 | stepheniii
Just how cold do you store your paste? And what are your solder paste reps like? Here they fall over each other giving support for their paste. And have you seen the problem with flux separation or have you only heard about it?
Electronics Forum | Tue Dec 08 08:52:42 EST 2009 | cunningham
How do people prepare there solder paste for screen print? We currently remove them from the fridge and mix them in a 500g solder paste tub mixer to mix the flux and paste together we waste to much paste at the moment as we only use the tub for 1
Electronics Forum | Mon Dec 14 18:45:08 EST 2009 | gregoryyork
why not use a paste where it requires no refrigeration at all cheers Greg
Electronics Forum | Tue Dec 15 00:09:26 EST 2009 | isd_jwendell
Which paste are you referring to?
Electronics Forum | Tue Apr 12 04:37:52 EDT 2005 | chandran
1.Can anyone explain to me what is the clean and non clean solder? 2.What is the standard solder paste height spec for stencils 4mils,5mils and 6mils? 3.Whatis the meaning for ROHS?
Electronics Forum | Tue Dec 08 11:55:28 EST 2009 | GSx
here some of them: http://www.mvent.com.ph/malcom/sps1.htm http://www.bikudo.com/product_search/details/116079/solder_paste_mixer.html http://www.japanunix.co.jp/ju_en/products/UM-103.html http://www.fancort.com/robotic/_solder_paste_mixer.html
Electronics Forum | Fri Jul 29 10:03:02 EDT 2011 | blnorman
At a previous location we used the Semco cartridges. Occasionally the operator would have to scrape down the stencil and knead the paste back in. That would keep the paste on the edges from drying out. It was just standard procedure.
Electronics Forum | Thu Dec 10 04:19:55 EST 2009 | cunningham
do you not have a problem with flux seperating from when it was chilled? due to our high mix low volume we really cant afford to have solder paste waiting for an hour or so till its ready before we can build