Electronics Forum | Sun Jul 04 19:49:05 EDT 2004 | indy
Hello Everyone, We are having some problem with Palladium-Silver surface finish. We have ceramic components with the above surface finish. When we try to assemble these on Sn/Pb solder, we are observing open joints. If we reflow the compt for more t
Electronics Forum | Thu Oct 18 18:39:15 EDT 2001 | davef
Responding to your questions ... RELIABILITY OF 1% SILVER SOLDER PASTE: It�s as good as the next solder paste, all other things the same. Look at your back articles by Jennie Hang in SMT magazine. I want to say she wrote an article on the topic i
Electronics Forum | Tue Jul 13 16:35:25 EDT 2004 | Richard
Sounds like your Si plalladium finish has oxide on it from the firing or sitting around too long. I used to assemble LTCC and have had plenty of dealings with this matter. The best and easiest is to get an active type flux and solder paste. AIM makes
Electronics Forum | Tue Aug 30 12:49:59 EDT 2005 | Ted
Slaine, We use a Pd/Ag thickfilm paste. Because of the leaching we had to start using solder pastes that have silver in it. For RoHS, we are using a solder paste with an alloy of Sn95/Ag05. We also have to double print the thickfilm pastes. I h
Electronics Forum | Thu Feb 17 21:42:12 EST 2000 | Dave F
Hey Bud: Moved from that Bi-crap to something serious, eh? Several things: 1 Get in touch with Doug Romm (drom@msg.ti.com) at Texas Instruments. He talks palladium. 2 Review the archives on Palladium. 3 I think you're running light on temps. Eut
Electronics Forum | Thu Feb 17 21:42:12 EST 2000 | Dave F
Hey Bud: Moved from that Bi-crap to something serious, eh? Several things: 1 Get in touch with Doug Romm (drom@msg.ti.com) at Texas Instruments. He talks palladium. 2 Review the archives on Palladium. 3 I think you're running light on temps. Eut
Electronics Forum | Wed Feb 20 09:38:47 EST 2002 | davef
Search the fine SMTnet Archives on � Sn62 � 62Sn � 2% Ag � 2% silver � 2Ag � etc re: "Do you have to use Tin/Lead/Silver paste only if the components are made from Tin/Lead/Silver ?" No Several points are: * Component leads with silver in the sol
Electronics Forum | Thu Dec 16 16:28:51 EST 2004 | Indy
Hi, We are using Sn/3.0Ag/0.5Cu solder paste on Pd/Ag pad metallization in one of our application. Could someone provide me information on the following: 1. How bad is the Leaching of Ag in SAC alloy and how it can be mitigated. 2. During reflow so
Electronics Forum | Tue May 23 09:50:37 EDT 2006 | flipit
They work well in silver conductive epoxy in hybrid applications. They are very poor in no clean applications. They don't work that well in OA solder paste either. Used them once in OA paste and in a nitrogen. They looked just fine. Solder to Pd
Electronics Forum | Mon May 22 18:19:29 EDT 2006 | Steve
I have read some threads about poor wetting on palladium-silver (Pd-Ag) coated components. I followed the suggestions, but I am still having a problem. The part is an 0603 chip type (Vishay varistor). The Process: solder paste is lead-free Alpha Met