Electronics Forum | Wed May 08 23:18:58 EDT 2002 | ianchan
Hi mates, have this SMT production issue : A) We have a leadless-chip-carrier(LCC) IC package that is classified under the Land-Grid-Array(LGA) package family. B) The LCC is 4mm x 4mm, and has 28 tin plated pads located beneath the outside perimet
Electronics Forum | Wed Mar 02 09:19:33 EST 2005 | Indy
we use SENJU M705. type3 solder paste. Has a good shelf life.
Electronics Forum | Sun Jan 18 09:20:26 EST 2009 | davef
We're not sure of the condition of your solder paste. So, afte 24 hours, if it's: * Unused, in a reclosed container, maybe a week of life depending on the environment * Used, scrap A simple coalescence test can quickly determine the condition of sol
Electronics Forum | Mon Feb 27 09:09:36 EST 2006 | davef
Silver on your copper or brass part is a solderability protection. The silver diffuses into the solder and you solder to the base metal, either the copper or brass in your case. Soldering to copper is well known. The issues are soldering to brass
Electronics Forum | Tue Aug 27 08:12:35 EDT 2002 | jmaruska
Do you have some experience with solder paste WS1208. What is the "best" conditions for printing process? I mean type of stencil, apertures, squeegee. Do you have original data sheet of this solder paste? - life time, working time on the stencil, sh
Electronics Forum | Wed Feb 07 21:58:38 EST 2001 | davef
We are reviewing our shelf life policy and have the following items listed as shelf life sensitive: Printed circuit boards, peelable solder mask, solder paste, moisture sensitive parts, multiwire printed circuit boards from Icon or Hitachi, NiCd batt
Electronics Forum | Tue Mar 03 07:47:48 EST 2020 | dontfeedphils
Thanks for the info. In a past life I ran everything WS and washed in a batch wash using saponifier. I'm surprised I never saw anything then as we would regularly wash boards assembled on only one side. Unless it's specifically washing in DI only.
Electronics Forum | Thu Jan 21 17:07:16 EST 1999 | ed zamborsky
I've had alot of success with the solder pastes from ESP in Rhode Island. They have great shelf life and are easy to print | I'm currently planning to do an evaluation of RMA flux solder pastes for mil type applications. Does anyone have any suggest
Electronics Forum | Thu Feb 27 16:23:37 EST 2020 | dwl
http://www.circuitnet.com/news/uploads/3/Comparing-Soldering-Results-of-ENIG-and-EPIG-Post-Steam-Exposure.pdf Years ago, I battled this problem. ENIG PCBs reflowed with active WS flux. We built one side, and then washed them because they were going
Electronics Forum | Wed Jul 07 13:33:45 EDT 1999 | Dave F
| who can tell me how viscosity measurements are really effective in smt process control? what can I monitor? Is it depending from fine pitch size? | Thanks a lot. | g. d'andrea | People write books on SMT process control. What's your problem? I