Electronics Forum | Tue Jun 09 15:46:29 EDT 1998 | Aric Parr
| Hi there Gary, | Your solder ball problem is very similar the problem I experienced, but I was using a water soluble paste at the time. It started by inspectors telling me that they were seeing cold solder on some SIMM's that we had built regularly
Electronics Forum | Mon Oct 21 22:15:36 EDT 2002 | davef
First, SIR data is heavily dependant on the test pattern selected. Be very careful when comparing the results of resistance readings taken from different geometric patterns. Second, if yer talkin': * Bare boards, yupper. * Finished assemblies impor
Electronics Forum | Sun Jun 13 05:46:21 EDT 1999 | Brian Ellis
Murray "No-clean" fluxes/pastes should not normally give "white residues". Before exploring cleaning, which is costly for small production levels, I suggest you may care to find out why you have these residues. To help you, can you please answer th
Electronics Forum | Thu Apr 05 12:25:01 EDT 2001 | davef
Talk about bucking the trend!!! OK, OK, I know some US military work still requires RMA. You�re both correct. Cleaning decisions for RMA fluxed boards are based on customers requirements. [Some do (clean) and some don�t.] Older US military speci
Electronics Forum | Sat May 29 16:56:26 EDT 1999 | Jeff Sanchez
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Sun May 30 10:15:34 EDT 1999 | Vic Lau
| | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a dou
Electronics Forum | Thu Jan 08 15:03:40 EST 2004 | dwzeek
We have an ongoing problem with our QFP144 packages soldering. It has not received much attention until late due to some customer failures. Most of the failures would show up in ESS testing and be repaired. The failure rate is about 2 in 1000 parts f
Electronics Forum | Sun Aug 08 04:36:02 EDT 1999 | Brian
Dave Frankly, I think you may be barking up the wrong tree. Like DaveF, I suggest that the process would be horrendously expensive with masking and so on. The $64,000 question is whether what you propose will serve any useful purpose. I venture to
Electronics Forum | Mon Oct 18 05:23:01 EDT 1999 | Brian
Steve What do you mean by better? More/less activity? fewer retouches? longer shelf life at ambient temperature? less hygroscopicity? longer open time on the stencil? easier to wash? easier to treat waste water? easier for washing machine maintenanc
Electronics Forum | Mon May 31 15:09:56 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi