Electronics Forum | Tue Jul 16 12:24:25 EDT 2019 | slthomas
In VERY general terms, water soluble flux is usually better at getting good wetting of the soldered connections unless you have a very well controlled process, in which case no-clean can be very handy (you don't have to clean). Water soluble flux re
Electronics Forum | Wed Mar 10 09:52:22 EST 1999 | justin medernach
| We are starting up an SMT line with a printer and convection oven.... The area we are considering for the printer is totally uncontrolled for humidity, temperature and even cleanliness. | | We are working on the filters to keep particulates down,
Electronics Forum | Mon Jan 19 20:25:52 EST 1998 | Steve Gregory
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Mon Nov 01 16:22:47 EDT 2010 | jax
Who Cares... Mix Away! Although you should not mix different Solder Pastes' together in a container or on a stencil (Mostly due to the flux, although solder sphere size and shape could cause an issue), mixing solder brands or chemistries on a board
Electronics Forum | Tue Feb 19 19:36:21 EST 2002 | davef
You weren�t clear but I assume the problem is not widely distributed and affects only a few parts on each board. Do this trick: * Cut a ~1� piece of fairly serious wire, like 18 or 12 AWG. * Strip the insulation. * Gear-up with gloves, glasses, and
Electronics Forum | Tue Aug 14 17:55:01 EDT 2001 | Boysen
Are you using a water soluble paste? Older generations of water soluble paste are notorious for voiding. Some of the new generation water soluble fluxes allow a much wider process window.
Electronics Forum | Wed Sep 26 12:16:44 EDT 2012 | bwjm
Hi Guys,recently i am facing an issue. Refer to the attached photo. This PCB is high RF speed, gold immersion single layer. After reflow, my solder seems to have black stains on it. I tried with SAC305 paste water soluble and no-clean, both results a
Electronics Forum | Tue Jun 26 19:51:31 EDT 2001 | davef
Rosin. A hard, natural resin, consisting of abietic acid [and pimaric acids in Europe] and their isomers, some fatty acids, and terepene hydrocarbons. Rosin is extracted from pine tree stumps. It�s an organic material distilled from oleoresin in p
Electronics Forum | Thu Aug 24 15:37:50 EDT 2006 | Chunks
Hi Any, This is from an earlies thread "Solder Ball After Reflow Process". Date: August 16, 2006 01:52 PM Author: Russ Subject: Solder Ball After Reflow Process Oven settings are meaningless here. What does the board see? It is the paste we a
Electronics Forum | Fri May 14 00:34:22 EDT 1999 | Mike D.
| I need some pics or documentation on how a finish soldered joint looks like for SMT component. I have various people who supposedly says has knowledge with High Temp says my joint could look better. The joint looks shiny and great except for a grai