Electronics Forum | Sat Jan 09 13:42:54 EST 2016 | aemery
Bill, Did you ever get this issue resolved? Electrovert is more my cup of tea, but I have completed a couple of pot replacements on the Vitronics waves. I remember on one machine after the retrofit the we were testing the machine and everything dro
Electronics Forum | Tue Dec 13 06:56:27 EST 2005 | adanhn
Hi Steve, What I came up with for our Soltec Sigma 6621 is to make a stainless steel wave solder bath insert.The insert with all its components eg. impeller, Chipwave assy, pump shafts, main wave assy etc. I will send for plasma nitride coating.Afer
Electronics Forum | Tue Aug 17 18:33:01 EDT 2004 | Hiram
Hi everybody, We are in the process of buying a new wave solder machine. Does anybody have experience working with Vitronics-Soltec (Delta wave 6622-CC for example)? What about Electrovert (Electra)? I would appreciate your feedback. Hiram
Electronics Forum | Sat Feb 22 11:37:00 EST 2020 | kylehunter
Hey all, I've made a post in the past about us expanding to a new space, but I wanted to do a new post with specific questions. We currently have a DEK 265, Phillips Opal Xii, and a Heller 1500. Our main reason for expanding is to have a lead-free
Electronics Forum | Tue Mar 15 18:42:57 EST 2005 | simmcircuits
Hi, Can anyone give me a bit of an advise or tip on how to reduce the flux residues on the board when it comes out of the wavesolder machine. The Vitronics Soltec 6622CC that we are using have been producing boards like this for years and people her
Electronics Forum | Tue Sep 15 13:02:55 EDT 2009 | horvath83
What do you think about optimal setup for 8-hour working shift and 16-hour standby time. What is the most energy efficient setup for standby time? Complete cooldown or maintaining temperature in solder pot?
Electronics Forum | Tue Feb 14 03:58:17 EST 2006 | Rob
Yes, it's fine - as Pete says you have to replace certain parts & either get the pot recoated or a new one. We ran a "Lead free" 6622C from Vitronics Soltec on Tin Lead, then it was cleaned up, recoated and loaded with a no-lead alloy with no proble
Electronics Forum | Wed Aug 18 00:41:15 EDT 2004 | Grant
Hi, We have the Soltec Delta C. It works well, and is very stable. I think the software is a bit simplistic, but it keeps the wave stable, so that's the main thing. It's the timer on the software that I find annoying. It has a warm up time, and yo
Electronics Forum | Sat Dec 02 11:35:30 EST 2006 | davef
Best dross remover is to not produce dross. Search the fine SMYnet Archives for previous discussions Dross will not increase signicantly * Another story, that lead-free solders will generate a greater volume of dross than conventional materials, is