Electronics Forum | Thu Jan 12 17:42:55 EST 2012 | warwolf
yeah we are getting quotes on a new solder pot, we have used that paint we tested a small sample of it with solder and it seems to be ok, we are doing a full solder alloy change in about two months so we will have a chance to inspect the solder pot a
Electronics Forum | Fri Feb 24 02:04:50 EST 2017 | soldertraining
Selective Soldering Frames can pull large amounts of heat from the solder wave at the point of contact, effectively lowering the temperature of the solder at the solder joint. You should confirm the temperature of the solder joints by running a therm
Electronics Forum | Wed Mar 11 19:22:02 EDT 2020 | victorzubashev
Hi, 1. do not use flux-cored wire- the smell is bad and flux will evaporate anyway at the time of solder wire melting. 2. as suggested use solder bars, something like this: https://smtnet.com/company/index.cfm?fuseaction=view_company&company_id=39635
Electronics Forum | Wed Aug 29 12:12:14 EDT 2018 | solderingpro
What type of flux are you using today? - Obviously you have already outlined the difference in the parent materials and parent material preparation, so using the same program/profile will not work; the characteristics are different. Try increasing p
Electronics Forum | Wed Aug 27 14:38:20 EDT 2008 | rgduval
Does your paste provider recommend a TAL? For the leaded and lead-free pastes that we use, the manufacturer recommends 60 seconds above liquidous. I note that your profile shows the TAL as 30 seconds, which may not be sufficient. That said, tho
Electronics Forum | Sun Sep 28 17:14:53 EDT 2008 | ronsou
small pads like 0402 tend to get hot quite > easily. looks like excessive heat is your problem > here. pads are wetted, component leads are not. > this means solder paste flux on top layer was > exhausted before entering in reflow. your profile
Electronics Forum | Tue Sep 02 15:29:36 EDT 2008 | bvdl
small pads like 0402 tend to get hot quite easily. looks like excessive heat is your problem here. pads are wetted, component leads are not. this means solder paste flux on top layer was exhausted before entering in reflow. your profile is the 'in-be
Electronics Forum | Mon Jun 05 18:50:10 EDT 2017 | caurbach
Hi Zac, My 2 cents: We had similar problems on a board in the same situation (tin-lead HASL, very long leads, low pot height, high pump RPM). Trimming the leads shorter, moving the pot closer to the board, and dropping the pump speed down to sane
Electronics Forum | Thu Aug 03 14:19:50 EDT 2017 | sumote
Looking at picture 20170801_095540.jpg, the leads look pretty long to me. This would cause you to have to lower your solder pot so that they don't get hung up. Have the leads cut to ~0.150" (0.200" max) long and then raise your pot up.
Electronics Forum | Thu Aug 03 17:53:58 EDT 2017 | zsoden
That may just be an optical illusion. I've just measured and they're cut to just over 4mm (0.157"). The pot is at the level specified by the manufacturer (5mm from the bottom of the PCB if I remember correctly).