Electronics Forum | Thu Sep 12 09:12:22 EDT 2002 | mhoughton
I have printed and placed similar devices in high volume with exactly this spec for a couple of years with no problems, are you using laser cut stencils and what type of solder paste are you using? and what is the end use of the product as it may nee
Electronics Forum | Thu Sep 12 09:15:29 EDT 2002 | mhoughton
I have printed and placed similar devices in high volume with exactly this spec for a couple of years with no problems, are you using laser cut stencils and what type of solder paste are you using? and what is the end use of the product as it may nee
Electronics Forum | Tue Mar 01 13:51:23 EST 2005 | pjc
pr is 100% correct, can't have visual inspectors touching up for the reason he states. I have always seen that- when in doubt they will always "touch up". Touching up is always a bad thing. Looks like you have some problems that need fixing to elimin
Electronics Forum | Wed Dec 13 13:11:06 EST 2017 | barryg
HI all. Recently we have been experiencing some PCB defects and so far it appears on a particular pcb. Components in areas, and the areas appears to be random, have shifted, skewed components. Most of these components, it appears the solder has flowe
Electronics Forum | Thu Jan 28 09:45:44 EST 1999 | parag
| | i am working with the noclean process and getting white residues on the bottomside of the board probably due to the | | wave soldering flux.i am using a no-clean solder paste and a noclean wave solder flux.The boards passed the accelerated tempe
Electronics Forum | Mon Jun 27 10:25:29 EDT 2005 | Paul
Hi Erik, looks like there's not much appetite for this debate on this forum. Possibly because not many use them and aren't in a position to confirm or deny what we know. We use our pumps 6 days a week, 24hrs a day so it's a very dynamic proc
Electronics Forum | Wed Dec 10 10:05:07 EST 2003 | davef
We do not have experience soldering to the PVD surface you plan to use. We use Titanium [Ti] stiffeners in wave soldering and our wave equipment manufacturer uses Ti fingers, nozzles, pump blades, and other parts, because solder doesn�t stick to Ti.
Electronics Forum | Mon May 24 10:45:04 EDT 1999 | John Thorup
| Can anyone help me with the correct baking cycle for removing moisture for PWB's. These are 10 layer double sided SMT. | | Thank You R. J. Klein Wassink in Soldering in Electronics states - 16 hours @ 105C or 40 hours @ 80C in a ventilated oven
Electronics Forum | Wed Jul 23 03:04:57 EDT 2008 | gfro
Hello, We are using a PCB with thickness 3.2mm 4 layer and lot of through hole via's of diameter 0.4mm. We specified our PCB vendor to do plugging. Now we have big problems, that after 1..4 weeks we measure a low resistance between track's/via's of
Electronics Forum | Fri Aug 19 06:49:27 EDT 2011 | leadthree
I got this MQFP-144 and the soldering looks always very flimsy. I think I use a suitable leaded paste (water-soluble) and the stencil thickness is also OK. The IC on the image looks a bit shifted, that's not the problem. The problem is rather that