Electronics Forum | Tue Apr 13 09:46:39 EDT 2004 | davef
Now, that's different. We misunderstood the problem from your original descrtiption. We thought the voids were showing at the via in the pad. Now, we understand the voids appear to be in the solder balls. Suggestions are: * Search the SMTnet Arch
Electronics Forum | Mon Aug 09 20:47:21 EDT 2004 | KEN
I think OA flux left on the pot would quickly looses its activity and become part of the dross waste stream, and smoke stream for that matter. Also, if your wave is setup properly your selective pallets will scour (push) the top of the lambda wav
Electronics Forum | Tue Jan 04 12:37:41 EST 2005 | Cmiller
We have been using this finish almost exclusively for fine pitch boards for about 5 years. Make SURE you use a board house that does the gold plating in-house. There are some potential issues as DaveF stated. The only problem we have encountered is w
Electronics Forum | Sat Dec 17 08:07:06 EST 2005 | grantp
Hi, What worries me is that a lot of people speak about what they have heard, but there is no firm facts on exactly what the situation is. I did a seminar on lead free a while ago, and was told that going lead free on the components while running l
Electronics Forum | Fri Feb 17 18:33:08 EST 2006 | mika
Paste In Hole "PIH" or Pin In Paste "PIP" are two different names of the same process. As far as I know this is fairly simple: the reason from the beginning is to avoid an extra process step/steps in the production line. That is to produce through h
Electronics Forum | Tue Mar 28 11:17:19 EST 2006 | smartasp
Thanks for the input Guys Yeah the not so knowledgable customer does not like to residues for cosmetic resons. The flux is for lead free process, of the no clean and water soluable type. We have explained to him that technically the residues do not
Electronics Forum | Fri Apr 07 17:44:07 EDT 2006 | ratsalad
I still have half of a 500 g jar of this paste left. I'm going to give it another shot, but my first experience was not so wonderful. Everything was great until we reflowed it. Our profile matched AIM's recommendation, as far as I can see. The ch
Electronics Forum | Sat Sep 08 08:55:24 EDT 2007 | davef
We expect to see a copper shadow along the edge of pads when soldering boards with organic solderability protection [OSP]. IPC-A-610 has defined this as acceptable for years. During early reflow stages, the flux in paste dissolves the OSP where ther
Electronics Forum | Fri Dec 28 17:44:41 EST 2007 | flipit
Back in the mid 90s I used an SVS 3D solder paste inspection system. We used it as a stand along unit but it was an inline model. We would bring printed PCBs off the Dek 265 solder printers and check every 5 or 10 printed panels. They almost alway
Electronics Forum | Thu Apr 17 05:14:40 EDT 2008 | gregoryyork
I have seen similar things like this before with Solder Resist redepositig back on the pads, this is a clear residue very hard to see. Solder resist will obviously resist solder adhering to it. If you rework the boards then the heat of the iron will