Avillaro, would you say that vapor phase process was selected, because the boards are so thick and heavy? I would assume so. Have you ever tried to run them through reflow oven? To understand better your challenge, we need to understand the setup be
Electronics Forum | Tue Sep 01 11:46:09 EDT 2009 | andoe
when the cp6 loads a board everything seems normal / as the table drops the pcb lines up onto the origan hole and then instantly fails with -- "original pin error" we have run this board before. any ideas? thanks
Electronics Forum | Thu Nov 07 21:28:31 EST 2019 | sssamw
The connector is so long, and has big metal parts, it will be little deformed during reflow I guess, andthe pins planarity should be critical for 200 pins. Did you measure the non wetting pins profile to see if temperature ok? And maybe you can try u
Electronics Forum | Mon Apr 03 16:41:40 EDT 2023 | dilogic
Well, this is a very odd bug - it turned out one of capacitors, defined as a no-lead, had pin definition changed to gull-wing! Interestingly, if that part was located on Head1, it won't cause machine hang-up...
Electronics Forum | Thu Jul 29 11:14:46 EDT 1999 | Justin Medernach
| I'm working on a prototype board that requires a 600 pin BGA. This is a metal top BGA being placed on a 11" x 17" PCB about .62" thick. | | The part is 1.77" square with a 50 mil pitch and 30 mil bump diameter. The bumps are located on the
Electronics Forum | Tue Jul 27 16:22:17 EDT 1999 | Earl Moon
| I'm working on a prototype board that requires a 600 pin BGA. This is a metal top BGA being placed on a 11" x 17" PCB about .62" thick. | | The part is 1.77" square with a 50 mil pitch and 30 mil bump diameter. The bumps are located on the
Electronics Forum | Tue Jan 14 19:41:32 EST 2020 | avillaro2020
Hi Evtimov, Thanks for your response. Yes, the vapour phase is suppose to handle big and heavy boards, at least thats the intention. Well our thin board is like around 3mm which is not really thin. In our application the thicker the boards means more
Electronics Forum | Tue Jan 14 11:39:51 EST 2020 | avillaro2020
Thanks Robl. I’ve contacted samtec followed their advice but ended up empty handed. Originally my stencil thickness is 6 mils, samtec stressed the need for the paste and charge to have good contact but this is challenged by the inherent charge non-co
Electronics Forum | Mon Jan 13 17:39:49 EST 2020 | avillaro2020
Hi, I need help on how to address the solder wicking on the samtec searay connector after reflow resulting to open solder joints on thick and thermal heavy PCB (4.4mm and 6.3mm). I increased my solder paste thickness to 8 mils, the connector is manua
Electronics Forum | Wed Jan 15 11:53:40 EST 2020 | avillaro2020
As far as the large thermal gradient I have on my thick and thermal heavy board, I've done quite a bit to minimize the gradient but not successful. it's like one pad is connected to a signal while the other pad is connected to ground, you can't bring