Electronics Forum | Sat Sep 09 08:21:36 EDT 2000 | Sal
guys Currently experienced this problem on a product which had been running satifactorily for a period of time. No process changes were made, The problem was highlighted when after ICT when the boards were loaded in to the stress chamber, after the
Electronics Forum | Mon Mar 12 10:29:07 EDT 2007 | george
Are you using wave solder pallets? I use same flux and solder as you do. I've seen this problem when some walls in the wave fixture cause a "shadowing effect"...if you enlarge those openings you will increase the dwell time eliminatting voids (if the
Electronics Forum | Tue Mar 06 14:10:52 EST 2001 | CAL
Are the voids in the balls of a BGA? Are you verifying this through x-ray if they are? some voids depending on size and location are some what accepted. Solder paste type? Solder paste date code? Humidity high? PCB's been stored in a truck trailer?
Electronics Forum | Wed Feb 28 19:44:50 EST 2001 | pzohbon
I am having problems with voids in our soldering process. I believe it to be the fact that we use a no clean flux without control on how the boards are handled (gloves, procedures, etc.) Does anyone have suggestions on the appropriate place to start?
Electronics Forum | Thu Mar 01 11:43:08 EST 2001 | dason_c
Not enough info, when you say no clean flux, is it for wave soldering process, please provide more detail, SMT or wave, is it all the joint which you find the void? Rgds
Electronics Forum | Thu Nov 01 10:57:34 EDT 2012 | kris1128
Has anyone heard whether the elevation of a plant can effect solder joint formation? One plant at sea level, one at 7,000 feet elevation... same equipment and profiles, big voiding defects at higher elevation. I did a search and found no similar post
Electronics Forum | Thu Mar 01 10:29:00 EST 2001 | davef
If the soldering process is not controlled, the results are variable, regardless of the flux type. Tell us more about your concerns, process, solder, etc
Electronics Forum | Fri Mar 02 08:52:20 EST 2001 | markkrmp
Are your voids looking like blow holes also? Is this only occurring on the solder joints of the Thru Hole components and Via's? Or does this happen on SMD pads? My experience is that we have seen this but only with some of our older PCB's which are
Electronics Forum | Tue Mar 06 03:29:05 EST 2001 | daled
Hello I am looking for any data that confirms the long term reliabilty of no clean paste as opposed to water soluable. Does anyone have any past experiences of problems when changing over from water soluable to no clean in the SMT prcocess?? Thanks i
Electronics Forum | Tue Mar 06 09:18:33 EST 2001 | davef
Two things: 1 Go to IPC and buy "TP-1115 - Selection & Implementation Strategy for A Low-Residue No-Clean Process - Provides direction to electronics manufacturers interested in adopting low residue (LR) assembly technology. It addresses the concern