Electronics Forum | Mon Apr 16 12:59:51 EDT 2001 | Mike R
If you will place a temperature strip on the board during wave soldering process you will get a max of 210 F or 98.8 C which is normal on the standard wave temperature. The problem on the 10% solder on the TH via hole can be caused by insufficient fl
Electronics Forum | Sat Apr 14 03:25:04 EDT 2001 | kpliew
Hi , As far as I experienced with wave reflow. If u have a refective thermal reader , u will see that the board is exposed to much more temp than the 120 deg that u set. Actually , once u see the board warp or comp. crack u should know that
Electronics Forum | Sat Apr 14 03:25:10 EDT 2001 | kpliew
Hi , As far as I experienced with wave reflow. If u have a refective thermal reader , u will see that the board is exposed to much more temp than the 120 deg that u set. Actually , once u see the board warp or comp. crack u should know that
Electronics Forum | Sat Apr 14 00:04:21 EDT 2001 | zam_bri
I'm not a Wave soldering guy and my friend have asked me a question on what is the best preheat time and temperature for Wave soldering.They experiences only 10% flow up thru the PTH barrel. I've asked them to increase the temperatue to 120 Deg C. Cu
Electronics Forum | Mon Jun 12 10:57:51 EDT 2000 | Jason
I am new to wave soldering. Any information is greatly welcomed. Here is the problem. After soldering the boards they have a film on the bottom of them and sometimes a white powder looking substance. I have tried decreasing the amount of flux on
Electronics Forum | Fri Jun 12 11:15:50 EDT 1998 | Ryan Jennens
Hey all! The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is on a pallet w
Electronics Forum | Tue Dec 11 02:44:26 EST 2001 | ianchan
SMT Experts, Hi, I have a pondering issue, which is : Our current specified Reflow preheat timing is a necessary 100~140sec for the ranges of 100~170Deg-C....obtained timing is 77sec... out of curiousity, if we further fine tune the obtained reflo
Electronics Forum | Tue Nov 17 03:04:38 EST 1998 | Charles Stringer
For some as yet unkown reason, we have started to have some boards sag and go under the wave. The boards are surface mount top side and conventional components wave soldered. We have checked the wave hight and both the profiles on the wave solder and
Electronics Forum | Tue May 17 10:11:54 EDT 2005 | russ
I would use a foam fluxer since spraying rosin will make the stickiest nastiest mess you can imagine. 18 layer board huh? You will want convection preheat, both top and bottom preheaters, preheat tunnel of at least 4-5', a chip wave, laminar flow w
Electronics Forum | Mon Jun 12 11:07:17 EDT 2000 | Jason
after reading some other problems i can tell you that we have an electrovert wave and are using alcohol base flux with convection preheaters. also we are spraying it on...not foaming. we are using an omega wave also. thanks again...if you need mor