To answer Gary's question: Gary, you will need a production board, thermal profiler, flux vendors product data sheet on the flux you intend to use, maybe your wave vendor service engineer or wave solder vendor contact (unless you know your wave) and
Electronics Forum | Fri Jun 23 12:32:20 EDT 2000 | Super K (Evil K)
To answer Gary's question: Gary, you will need a production board, thermal profiler, flux vendors product data sheet on the flux you intend to use, maybe your wave vendor service engineer or wave solder vendor contact (unless you know your wave) and
Electronics Forum | Tue May 23 03:40:20 EDT 2017 | bukas
the problem I had with pump was that turbine intake was eached by alloy. when I repaired intake, it was a irregular hole about 32mm in diameter, mechanics welded piece of plate with a 24mm hole (that was a factory size) we had to reduce pump speed fr
Electronics Forum | Mon Apr 19 11:36:10 EDT 2010 | baildl632
We installed a fixed distance optical sensor above the conveyor rail and "wired it" throught he machines terminal bus to cut the pump on only when a board was present at the pot. We also installed a timer in line so the pump would only stay on long e
Electronics Forum | Thu Mar 30 04:42:28 EST 2000 | cpgoh
HI all, thanks for the advise.. Electrovert is being used from 7am to 7pm and we do dedross from the surface of the solder bath during lunch time around 12nn. Break Time we just sweep them to the side.. Every two week, we do the solder bath maintena
Electronics Forum | Tue Jul 29 13:35:48 EDT 2008 | grics
We only use one type of flux for Lead Free. It is an alcohol based no clean flux. Is the wave shape and speed as large a factor in ive soldering as in traditional wave soldering? When you say "decrease the Z" do you mean the nozzel or solder heigh
Electronics Forum | Tue Jul 29 13:09:26 EDT 2008 | gabriella
Hi, for this kind of issues I will always go with the flux first. Are you using only one type of flux? Is it alcohol based or water based? Do you apply a good quantity? Second I will go with the wave shape and speed, and last will be the temperatur
Electronics Forum | Fri Mar 29 10:11:02 EDT 2019 | cyber_wolf
“For a number of years now, work has been proceeding in order to bring perfection to the crudely conceived idea of a transmission that would not only supply inverse reactive current for use in unilateral phase detractors, but would also be capable of
Electronics Forum | Mon Apr 03 01:17:37 EDT 2000 | cpgoh
I ever thot of changing the whole solder pot altogether but then it prove to be a costly measures.. If looking at the source of the problem, it might be mainly due to the way that the machine had been maintain... Anyone care to share how they are per
Electronics Forum | Thu Mar 30 11:07:41 EST 2000 | Wolfgang Busko
> the dirty patch appear seems to be a bit powdery on top of stickiness > the "harden" dirt in the solder pot or at pump are ususally "knock" out while cleaning.. is that thorough enough..? Assuming that 1) is true it might not be thorough enough. On