Electronics Forum | Wed Jan 10 09:30:23 EST 2018 | buckcho
Hello, which type solder paste are you using?
Electronics Forum | Thu Jan 11 11:29:58 EST 2018 | mohammad
I use this one Chip Quik Inc. SMD291AX250T3
Electronics Forum | Tue Jan 23 02:50:57 EST 2018 | buckcho
8 hours @ 20-50% RH 22-28°C (72-82°F) >4 hours @ 50-70% RH 22-28°C (72-82°F)
Electronics Forum | Sun Jan 07 07:40:31 EST 2018 | mohammad
Hi everybody. I'm new at SMT soldering. I'm using a stencil to print solder paste on PCB. and my board has 0402 components that it make assembling process long so I can't complete a set of board in a day and I have to continue in the next day. what
Electronics Forum | Sun Jan 07 08:46:08 EST 2018 | spoiltforchoice
Your paste should specify a number of times it is OK for various things to happen. The two you might care about are the "Stencil Time"/"Working life", which is how long the paste can be out of the pot on your stencil while you print PCBs. The othe
Electronics Forum | Fri Mar 21 11:10:24 EST 2003 | davef
There is no standard. If your boards solder well, they're good. Well soldered boards that have been stored a long time will have field life similar to well soldered boards that have not been stored a long time. The solderability of boards depends
Electronics Forum | Mon Jul 26 20:31:59 EDT 2010 | engr
When hand placing SMT components what is the working time before the solder paste become unusable (dry)?
Electronics Forum | Thu Apr 12 20:27:10 EDT 2001 | davef
Tantalum caps degrade over time. You should not be seeing "chipped-off & cracks" regardless of the age. This should not be a shelf-life issue, unless you are storing them in an aquarium. Tell us the story. Solderability is a shelf-life issue and
Electronics Forum | Tue Jul 02 16:04:08 EDT 2002 | russ
We normally disregard what the "tech" sheets say. A lot of it has to do with your printer settings, prints per hour, placement time, stencil cleaning procedures etc... Just another wrench to throw in, We have noticed lot to lot paste differences al
Electronics Forum | Fri Apr 25 04:44:56 EDT 2008 | jkhiew
Hi all, I mean after post adhesive oven curing (SMD at bottom side) prior to manual insert of PTH components (top side), what is the recommended storage time prior to wave soldering in order to avoid pin/blow holes and sunken joints issues (pcb asse