Electronics Forum | Thu May 20 07:53:55 EDT 1999 | Chris Nuttall
| | We care currently running into problems during our plug via process: | | At the moment we plug prior to soldermask (LPISM) using epoxy resin - plugging takes place from the component side - however we are seeing solderballs after solder level.Thi
Electronics Forum | Mon May 10 15:49:52 EDT 1999 | Steve Gregory
| | Can anyone tell me what the recommended "typical" cooling rates are after reflow? Are the cooling rates considered as critical to control as the heating rates and why/why not? | | I do not think there is a "typical" post reflow cooling rate out
Electronics Forum | Wed May 12 10:29:25 EDT 1999 | Timothy O'Neill
| | | Can anyone tell me what the recommended "typical" cooling rates are after reflow? Are the cooling rates considered as critical to control as the heating rates and why/why not? | | | I do not think there is a "typical" post reflow cooling rate
Electronics Forum | Fri Apr 30 15:24:12 EDT 1999 | Kevin Hussey
| Ok folk's has anyone used Alpha Metal's UP78 solder paste ? | | Our place is looking to move to that as the way to go, getting rid of the Hereaus 362's and Alpha 737's of the current set up. | | My question's are really : | how is the printabilit
Electronics Forum | Tue Jun 09 15:46:29 EDT 1998 | Aric Parr
| Hi there Gary, | Your solder ball problem is very similar the problem I experienced, but I was using a water soluble paste at the time. It started by inspectors telling me that they were seeing cold solder on some SIMM's that we had built regularly
Electronics Forum | Thu May 26 16:41:00 EDT 2011 | scottp
Here's what I do: - Test Surface Insulation Resistance (we're in the high reliability market and use a test significantly harder than IPC's). I also test SIR in combination with other assembly materials like conformal coatings and wave solder flux
Electronics Forum | Wed Sep 22 22:23:55 EDT 1999 | SY
| | | | | My stencil thickness is 6 mil and we got qfp's with fine pitch. | | | | | how many percent should i reduce my stencil aperture using a 6 mil stencil for 0.5 mm pitch and 0.4 mm pitch ? | | | | | | | | | | thanks | | | | | | | | | We use 6
Electronics Forum | Fri Aug 06 06:13:37 EDT 1999 | Wolfgang Busko
| | | | | | | | | | | | | | | | | | Hello, | | | | | If you are using no-clean and they are entrapped in the flux it is also IPC accepted but i havent found a customer yet who agrees with that. Im sure you have checked your profile. I had the same
Electronics Forum | Tue Jun 29 04:45:10 EDT 1999 | Earl Moon
| | Hey there gang, how's it going ? | | | | Anyway's here's my probelm, got a new product to build double sided reflow, lot's of so20's and PLcc's 1206's, 0805's the usual stuff. Probelm is all the pad spacing of the 1206's are too big, my componen
Electronics Forum | Fri May 14 12:01:40 EDT 1999 | Chrys Shea
| | | I am looking for anyone who has converted over to VOC Free flux. I need some info on any problems, etc. that you might have had. | | | | | | Please E-mail me at wes.ruggles@vickers-systems.com or call at (513) 494-5229 | | | | | | Thanks | |
.jpg)