Electronics Forum | Thu Nov 04 11:56:33 EST 1999 | Tim Almy
Is 260 degrees C / 500 degrees F the optimum temperature for wave soldering ?
Electronics Forum | Tue Oct 19 10:53:14 EDT 1999 | Carol Zhang
Hi, I tried to use high temperature solder (540 - 570F)to connect four spacers on the board. The solder mask around the spacers wrinkled a lot.I can even see a few bulbs around it. I use hot plate and solder rings. After hot plate is heated to appr
Electronics Forum | Thu Jun 03 09:40:20 EDT 1999 | Ryan Jennens
In a month or so, we will be getting an in-line x-ray inspection machine. It will require that we solder our most comlicated side (normally top) first. This is opposite to our process now where we solder our passive (bottom) side first. We cannot
Electronics Forum | Sun Apr 04 11:25:21 EDT 1999 | Cuch
I need help in finding solder paste measuring equipment.
Electronics Forum | Wed Feb 17 09:51:43 EST 1999 | Al
We have problems with solder balls after reflow. Anybody have any ideas as to what causes them?
Electronics Forum | Fri Dec 11 11:06:23 EST 1998 | Lyle Sherwood
DO you know of an Industry Standard that describes solder paste geometries requirements?
Electronics Forum | Mon Oct 19 07:25:38 EDT 1998 | Greg Flynn
Has anybody out there, heard of a process/technology called AZOTE SOLDERING ???
Electronics Forum | Wed Oct 14 18:26:21 EDT 1998 | Abhijit
How are solder pastes manufactured right from the level of extracting lead and tin ?
Electronics Forum | Thu Sep 17 07:06:15 EDT 1998 | joakim fagerlund
We have problems with voids when we solder lids to ceramic flatpackages. The sealring of the package is gold(100 micro inches or 2.5 micro meters)with a underlayer of Nickel The solder is attached to the lid (preform) and the solder material is Au/S
Electronics Forum | Wed Sep 16 08:46:50 EDT 1998 | Chrys
Hi Folks, Need to draw upon the vast expertise in this forum... Whenever you fill a new wave solder machine with fresh bar solder, it seems to produce more than the normal amount of dross for a few weeks. I always understood this to be the solder "c