Electronics Forum | Mon Oct 19 07:39:15 EDT 2009 | m_imtiaz
Hi, We are facing solder ball problem in manual soldering process (between wire and terminal). we are using no-clean solder (63:37)and temperature setting in iron is around 400 Cel. Can any one suggest me how to solve this problem Any thoughts would
Electronics Forum | Mon Oct 19 15:08:14 EDT 2009 | markhoch
Would be glad to offer some assistance, but I've got a couple of questions first: 1) What type of supplemental flux are you using? (If any) 2) Is your problem consistent across all assemblers, or can you trace the assemblies with solder ball issues b
Electronics Forum | Sun Jun 01 03:42:49 EDT 2014 | sync40
Hello to everybody in this forum, I would like to know any information that you kindly may have about the following subject: We very often do manual soldering assembly of immersion tin finished PCBs. Since thiourea is used in the formulation of the
Electronics Forum | Mon Jun 02 15:51:17 EDT 2014 | sync40
Thank you so much again davef for your new reply. This past weekend I was looking for more information regarding this subject, but, as you stated there is no information about thioruea concerns during assembly soldering operations, mainly focused in
Electronics Forum | Mon Jun 02 15:09:10 EDT 2014 | davef
I've never heard of anyone affected by thiourea during assembly soldering operations. I believe the greatest concern of exposure to thiourea is during the board fabrication process. BR ... davef
Electronics Forum | Sun Jun 01 13:50:12 EDT 2014 | sync40
Thank you for your reply davef. Although the US restriction, I think that there are plenty of users of immersion tin in Americas, mainly low-volume fabs that do not plan to outsource finishing, or do not plan or can not invest in a HASL. If we res
Electronics Forum | Mon Jun 02 20:38:42 EDT 2014 | davef
I believe that you get better responses when you start a new thread, but that's just an opinion, not a rule. BR ... davef
Electronics Forum | Sun Jun 01 13:25:26 EDT 2014 | davef
Eurolanders and Asians are the primary users of immersion tin. In the US, the use of immersion tin is restricted due to the concern over the thiourea that used in tin plating process. Thiourea is a suspected carcinogen. I’m inclined to say, “aww, as
Electronics Forum | Wed Feb 24 03:49:08 EST 2021 | bangir
Hello Dear... I am looking for Manual Book/Part List for Solder Print Inspection DJTECH BPC707ADX. Please share me the manual book.. Thanks, BangIr
Electronics Forum | Mon Dec 22 12:14:15 EST 2008 | pcbbuilders
we sometimes have problems with solder paste release. we use a manual stencil printer. does anyone have any thoughts on using two passes of solder paste on the stencil? i have found that running the second pass gives me better deposits on the fine pi