Electronics Forum | Sat Nov 08 10:04:26 EST 2003 | severs
Once you have selected your plating based on electrical and physical requirments, you should know that there is an inexpensive plastic storage packaging developed by Lucent which can keep any platings solderability from degrading for up to 10 years o
Electronics Forum | Sun Mar 08 08:07:20 EST 1998 | jerry
Who can deliever the stainless steel for SMT stencil
Electronics Forum | Sat May 07 04:40:04 EDT 2005 | grayman
Hi, There are many companies shifting lead free solder wave. My question is can anyone give me idea if we can still use our old solder wave machine for lead free eventhough the solder pot is stainless steel 316L? Our solder bath has titanium nozzl
Electronics Forum | Mon May 09 09:02:17 EDT 2005 | davef
Your 316L stainless steel pot will not contain lead-free solder, over the long term. We'd bet that our solder machine equipment manufacturer will "swap" you a lead-free solder compatable pot for your current pot.
Electronics Forum | Fri Nov 07 15:57:56 EST 2003 | Marc Simmel
Are there specifications or recommendations for electro-deposited tin-lead plating thickness on austenitic stainless steel that would provide a shelf life of 1 year? 6 months? Would 2 to 3 microns (78 to 118 micro-inches) 90/10 tin-lead over 1.27 mi
Electronics Forum | cyber_wolf |
Mon May 09 11:10:10 EDT 2005
Electronics Forum | Mon May 09 08:31:23 EDT 2005 | jdengler
Grayman, You might want to read this paper. http://www.speedlinetech.com/docs/Equipment-Lead-Free-Wavesoldering.pdf Jerry
Electronics Forum | Wed Jun 29 03:37:53 EDT 2005 | lupo
Hi, I think that the time depends on the type of stainless steel, temperature and solder alloy. For example, one of our machines is delivered with 316 stainless pot and alloy SnNi. It worked six months (120days*16hours = 1920hours) and aft
Electronics Forum | Fri Jul 08 09:57:31 EDT 2005 | fctassembly
Proy, Another issue is what exact formulation of SAC is used. Much of the SAC305 being used in Asia contains phosphorus, which is added in an attempt to reduce the heavy drossing that SAC305 produces. Phosphorus acts as a flux on steel so will increa
Electronics Forum | Sat Feb 12 10:33:31 EST 2000 | Francois Racine
First I'm a french people so excuse my bad english writing. I have a complete smt production line. First a screen printer DEK 240, a chip shooter PANASERT MVIIV, a multifonction machine MULTITRONIKS EP6000, a reflow oven at the end of the SMT line a
winsouce.jpg)