Electronics Forum | Mon Apr 03 23:17:51 EDT 2000 | Brian G
We have been experiencing intermittent problems with the solder masking bubbling up from the bottom side of the board, after wave soldering. Our board fabricator claims that none of his other customers are experiencing this problem, and that it is pr
Electronics Forum | Tue Dec 07 16:34:54 EST 1999 | Russ
Wolfgang, I appreciate your continued feedback! The main reason that I shortened the Time Above Liquidous (TAL) was it appeared that I was burning off all of the flux from the paste. By shortening the TAL to 45 seconds and decreasing peak temp to
Electronics Forum | Wed May 12 12:11:54 EDT 2004 | solderpro
Bruce, regards to all who are trying to help and have great input, with those type of lead length, I would be very impressed to see you get rid of the problem, and as the others said, no clean in a foam fluxer, not good but workable.... the real issu
Electronics Forum | Wed Jul 09 04:57:11 EDT 2003 | Matt Kehoe
Our company applies solid solder to surface mount lands. While processing a micro BGA design we had some pads fall off, peel, whatever you might call it, from the surface of the board when touched "GENTLY" with the tip of a blade to remove a small s
Electronics Forum | Sat Sep 18 12:27:21 EDT 1999 | Earl Moon
| | | Dave, I'll respond by paragraph: | | | | | Brian: | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slathered shiitake
Electronics Forum | Sat Sep 18 04:42:52 EDT 1999 | Brian
Dave, I'll respond by paragraph: | | | Brian: | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slathered shiitake burritos through
Electronics Forum | Sat Sep 18 14:37:00 EDT 1999 | Earl Moon
| | | | | | | | | Dave, I'll respond by paragraph: | | | | | | | | | Brian: | | | | | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like
Electronics Forum | Sat Sep 18 13:05:57 EDT 1999 | Brian
| | | | | | Dave, I'll respond by paragraph: | | | | | | | Brian: | | | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slath
Electronics Forum | Thu May 26 16:41:00 EDT 2011 | scottp
Here's what I do: - Test Surface Insulation Resistance (we're in the high reliability market and use a test significantly harder than IPC's). I also test SIR in combination with other assembly materials like conformal coatings and wave solder flux
Electronics Forum | Wed Jul 09 16:01:10 EDT 2003 | russ
Mike, the one pad that is "small" definitely appears to be over etching (It looks like it was supposed to be much larger). What is the dims of this little bugger as compared to the Gerber? i would also tend to believe that there probably is some mask