Electronics Forum | Sun Jul 26 07:52:35 EDT 2020 | sync40
Hello to everyone, Have you ever experienced soldermask bubbles inmediately after printed the soldermask itself? (for screen printing method of LPISM). I am not talking here about blistering or any outgassing defects after exposing to high temperatu
Electronics Forum | Sun Oct 01 23:58:55 EDT 2000 | stuartfd
Dear forum types, 1st timer so be good. I have a customer in China using Coates soldermask that in its self is not a problem. The problem is the flux their using, I think,it appears to have a vary high viscosity. The problem they have laid at my door
Electronics Forum | Mon Feb 21 11:22:21 EST 2000 | K. Ckak
Hi Kurt, I agree with Dave F. I had exact same problem with PBGA placement. We requested our PCB vendor to plug/tent via (button printing) after HASL with SR1000 which worked well in the long run. There are couple of failure modes associated wit
Electronics Forum | Mon Feb 21 11:22:21 EST 2000 | K. Ckak
Hi Kurt, I agree with Dave F. I had exact same problem with PBGA placement. We requested our PCB vendor to plug/tent via (button printing) after HASL with SR1000 which worked well in the long run. There are couple of failure modes associated wit
Electronics Forum | Fri Sep 10 11:45:09 EDT 1999 | Scott S. Snider
| scott. | I appreciate your sincere answer. | would tell me the hint about printer if i's possible | To tune our smt process we have to know what is the major X's | for defect. To know major X's with DOE we need a good measurement equipment.