Electronics Forum | Wed Jan 02 12:32:24 EST 2002 | cebukid
What is the rule-of-thumb on wave profiling Ceramics? I've used 2 methods: 1.) putting the T/C on the lead, and get a pretty good delta (within 50-80 deg. before hitting chip wave), well within manufacturer's spec. 2.) Right on the part body.
Electronics Forum | Thu Jan 10 06:52:51 EST 2002 | Dreamsniper
I'm using Kic Profiler and aluminium tape from Kic and thermocouples from Kic. They are good and reliable. I even manage to modify my heller 1088 by adjusting the fix conveyor and re-baffling the oven. Had dropped my 20-22 deg. C delta T down to 4.3
Electronics Forum | Fri Jan 11 11:14:14 EST 2002 | leedianeh
I am going to be using large numbers of silver immersion PCB's for assembly. I am concerned about long term storage ( shelf life )and handling prior to placement/assembly. The recommended 'shelf life' appears to be 6 months but obviously this will
Electronics Forum | Wed Mar 20 00:55:01 EST 2002 | ianchan
Heyz...at this rate i'am losing my mind too! We have been doing the "looks good; look bad" approach, and backed it all up with Z-height paste measurements. Only thing there's this customer QA asking how we established those USL & LSL utilized in our
Electronics Forum | Thu Mar 28 08:27:56 EST 2002 | davef
Don't be concerned. Brian and Neil don't allow us to link directly to email from SMTnet [even though from the way the link changes color you'd think you could. They do this to subjugate the huddling masses and lord the power of cold fusion over us.
Electronics Forum | Wed Apr 10 11:46:28 EDT 2002 | mlovett
I would like to know the Stated Specification for PTH size tolerances. Or is there a generalised acceptable limit?. We have some PCB's with hole sizes that I consider to be way off what I would deem acceptable, ie Finished hole size should be 0.89mm
Electronics Forum | Sat Apr 20 01:25:39 EDT 2002 | lysik
It is not just the rgistration fee. It is the fact that often after you register the machine you sre still denied a certian portion of service. UIC is very in check with their registration pricing. OEM's do however have a clause that says we can not
Electronics Forum | Tue May 07 07:29:24 EDT 2002 | Yannick
Hi, I reaaly mean AG (Like silver) we was thinking about going with immersion gold butis a bit more expensive. we use a no-clean paste but in a few year( maybe 1-2) we suppose to change to a lead free. You said that with Immersion gold we
Electronics Forum | Wed May 08 11:07:54 EDT 2002 | Carol Stirling
We have a concern with moisture absorbtion/humidity effects on PWBs specifically used for automated SMT (including BGA). I'm sure there is a IPC spec on this and would appreciate the number - I've searched the IPC web-site -no results. Could you t
Electronics Forum | Tue May 28 17:33:31 EDT 2002 | wilcoxito
We are just getting started doing BGA assembly at our plant. Any helpful hints would be greatly appreciated. My first main question is about stencils. We are considering using diamond shaped holes for the BGA pads. Does anyone have any experience
.png)