Electronics Forum | Thu Jul 20 13:28:13 EDT 2000 | Bob Willis
On all the trials I have done I have made no changes to the stencil thickness or apertures than the normal changes we make for our process. I have not changed any thing in terms on volume of solder for more reliable joints. I fact I have not read any
Electronics Forum | Thu Jun 17 19:40:11 EDT 1999 | Scott Cook
| first of all what is the technical term for the small amount of solder on a plated pad. we are getting poor screen printing gasketing on a 20 mil qfp due to this solder not being even or too high in spots and not covering the length of the pads. an
Electronics Forum | Thu Jun 17 19:40:27 EDT 1999 | Scott Cook
| first of all what is the technical term for the small amount of solder on a plated pad. we are getting poor screen printing gasketing on a 20 mil qfp due to this solder not being even or too high in spots and not covering the length of the pads. an
Electronics Forum | Thu Jun 17 19:41:29 EDT 1999 | Scott Cook
| | first of all what is the technical term for the small amount of solder on a plated pad. we are getting poor screen printing gasketing on a 20 mil qfp due to this solder not being even or too high in spots and not covering the length of the pads.
Electronics Forum | Wed Oct 02 09:36:10 EDT 2002 | scottefiske
Dragon, Was recently responsible for No Clean Process/Material evaluation and implementation project. Shop was 100% Water soluble facility. Several Top Paste manufacturers were invited to participate. (3) were evaluated. All key variables were identi
Electronics Forum | Thu Jul 17 20:46:55 EDT 2008 | davef
Which type? * Solder beads (mid-chip solder balls, attached to the waste line of your chip caps and resistors) This is more paste volume related. * Solder balls that tend to be more randomly scattered (as in spattered)? This tends to be more profile
Electronics Forum | Thu Mar 01 08:55:35 EST 2001 | Dale Dolan
We are currently reviewing the stencil cleaning process in house, we curently use ISOPROPYL ALCOHOL followed by a rub down with non lint wipe alls ( not good !!).As for drying the screen's, the apertures are blown out with compressed air and left to
Electronics Forum | Fri Apr 13 22:56:02 EDT 2001 | gdstanton
I've been chipping away on a solder bridging and poor fillet wetting problem for a few weeks now (new to the company) and I found two issues. First, after a review of stencil inventory, I found apertures to be oversized when compared to suggested di
Electronics Forum | Mon Jun 18 10:14:30 EDT 2001 | surachai
HI ALL; I WOULD LIKE TO KNOW THAT ANYBODY CAN RUN GLUE PRINTING PROCESS WITH 0402 CHIP AND PASS THEM TO WAVE SOLDERING PROCESS ,PLEASE GIVE ME THE INFORMATION ABOUT THEM . 1)HOW WIDE OF APERTURE DO YOU OPEN ON YOUR STENCIL? 2)HOW MANY YIELD OF THIS P
Electronics Forum | Mon Nov 01 22:16:04 EST 1999 | Dean
Without a detailed description of the suspect parts It is difficult to pin-point the exact solution to your process problem. However, whenever possible avoid non-value added additions to your current process. Here is the reality of the situation: