Electronics Forum | Thu Jul 31 15:41:23 EDT 2003 | davef
Q: Could any of you guys tell me what exactly is this greenish thing ? A: No, but is not copper oxide. Copper oxide is brown, the color of a penny [here in the US] or an untreated copper laminated trace on a board. Many copper salts are greenish in
Electronics Forum | Wed Dec 10 10:05:07 EST 2003 | davef
We do not have experience soldering to the PVD surface you plan to use. We use Titanium [Ti] stiffeners in wave soldering and our wave equipment manufacturer uses Ti fingers, nozzles, pump blades, and other parts, because solder doesn�t stick to Ti.
Electronics Forum | Thu Aug 12 18:06:09 EDT 2004 | SR
May I ask what component types you are using and who the suppliers are? FYI - If the components have exceeded their shelf life, they may have oxidized too much for soldering using low activity fluxes. Thanks and best regards, SR
Electronics Forum | Fri Jun 18 13:48:37 EDT 1999 | Earl Moon
| We currently use HASL on all of our boards and I would like to move to something else. I have sampled some boards with Entek OSP and I loved it, the problem is we have plated mounting holes on just about every board we make. Does anyone have info
Electronics Forum | Fri Jun 18 12:50:32 EDT 1999 | jseagle
We currently use HASL on all of our boards and I would like to move to something else. I have sampled some boards with Entek OSP and I loved it, the problem is we have plated mounting holes on just about every board we make. Does anyone have inform
Electronics Forum | Tue Jul 13 16:35:25 EDT 2004 | Richard
Sounds like your Si plalladium finish has oxide on it from the firing or sitting around too long. I used to assemble LTCC and have had plenty of dealings with this matter. The best and easiest is to get an active type flux and solder paste. AIM makes
Electronics Forum | Thu May 31 01:20:58 EDT 2012 | robertwillis
This is common and not an issue it is just the surface oxide Bob Willis
Electronics Forum | Fri Jul 10 07:34:00 EDT 2020 | elijah
From the poor bonding strength of the board, the surface quality problems of the board are divided into: 1. The cleanliness of the board surface; 2. The problem of micro graphite (or surface energy) on the surface. PCB circuit board proofing Youke bo
Electronics Forum | Wed May 30 10:09:39 EDT 2012 | brettrenishaw
Recently we have noticed a purple-blue colour film on the surface of the molten solder. It can be cleared when de-drossing the pot. The pot will normally go a yellow/gold colour before it turns purple-blue. Is this most likely an oxide of the tin or
Electronics Forum | Wed Apr 07 22:15:31 EDT 2004 | davef
We're not familiar with the AUG5 from Taiyo. [It doesn't show on their US site.] Is it liquid photoimageable? Printed solder masks are more likely to bleed. But you wouldn't have any solderability with bleed. Your plating seems acceptable [if th
The SMTA membership is a network of professionals who build skills, share practical experience and develop solutions in electronic assembly technologies and related business operations.
Training Provider / Events Organizer / Association / Non-Profit
6600 City W Pkwy
Eden Prairie, MN USA
Phone: 952-920-7682