Having the last two zones at the reflow temp (spike) is typically done on long ovens (10 zone) running at high conveyor speeds. This enables you to achieve peak temp and TAL as per the solderpaste specs at high production rates. Concerning reverse sp
Electronics Forum | Mon Nov 06 19:15:57 EST 2006 | Jerry Butters
The "marketing geniuses" of the world are now touting lead free ovens, lead free irons, and even lead free smocks, heel straps, and even G-Strings! Bottom line is - ya just gotta get it hotter, stupid! There's nothing "RoHS" about equipment besides
Electronics Forum | Mon Sep 29 16:38:07 EDT 2014 | rgduval
These papers are a good place to start when learning about profiling: https://www.smtnet.com/library/files/upload/374_RSS_vs_RTS_revised_12-99_(no_pics).doc http://www.ipcoutlook.org/pdf/best_practices_reflow_profiling.pdf If you're having a lot o
Electronics Forum | Fri Jan 24 09:52:08 EST 2014 | davem
Hi Guys, So I work for a small contract manufacturer which caters mainly to the defense sector. As such, our customers haven't (yet) had a great need to incorporate 01005's into their designs. Looking forward, we decided to "take the plunge" and dia
Electronics Forum | Mon Dec 06 12:37:57 EST 1999 | Russ
Christopher, in response to your request concerning if I have the same issue using OA fluxes the answer would be no. This finish works well with all of our current Water Soluble fluxes. As a note, I have done some further testing and so far it see
Electronics Forum | Tue Dec 07 08:11:04 EST 1999 | Wolfgang Busko
Hi Russ, there�s something I don�t understand about the measures you took. I guess that TAL means time above liquidous and shortening of that time can result in bad dissolution of the protective Au-layer. The necessary time for the Au to mix with you
Electronics Forum | Mon Nov 21 16:29:02 EST 2005 | pjc
Here is Manix web site: http://www.manixmfg.com/ Yes, the zone temps can be set high, but the thermal transfer efficiency is very low. I was profiling one of these ovens last week. To get 215C on the board you have to set the zone temp well over 30
Electronics Forum | Sat Apr 15 09:07:22 EDT 2006 | samir
Amol, We pulled off this "hybrid profile" with a leaded solder paste. We recently got our tensile test report results, and our Pb-Free BGA / Pb Paste sample broke off during tensile tests at the pad/substrate interface, and not the joint. This ind
Electronics Forum | Fri May 26 03:58:07 EDT 2006 | dave
Hi, We have a 5 zone oven and we use a RTS Profile. Our last zone is the zone that the reflow takes place. some basic analysis is as follows: TAL 70 secs, peak temp 210,ramp rate seems fine. A typical setting is : Z1 140 Z2 160 Z3 160 Z4 185 Z5 220
Electronics Forum | Wed Aug 16 13:52:24 EDT 2006 | russ
Oven settings are meaningless here. What does the board see? It is the paste we are concerned about not what the heaters are running at hehe. These solder balls are at the end of pad, which end? under the part or away from the part. I believe you