Electronics Forum | Mon Dec 06 03:54:57 EST 1999 | Chris May
Hi Russ, I have a similar situation. I have been told that this can be caused by the nickel, over which the gold is plated, can result in suspect joints, embrittlement etc. Some joints can even be weak and broken without much force on some of my boa
Electronics Forum | Tue Jul 03 01:54:42 EDT 2018 | rdhiman1
Reaching out to all conformal coating experts, please help! While setting up conformal coating using the automated atomized spray, we observing issues associated with conformal coating wetting on the following regions: 1) Component edges 2) Metalli
Electronics Forum | Tue Dec 08 18:40:04 EST 1998 | Graham Naisbitt
Hi all, Only observation I would make is that it depends upon what you term as clean? Now isn't that an old thorny question. Care to comment? Regards Graham | Hey there Dave! | | We used to use a batch cleaner when we used water-clean paste.
Electronics Forum | Sat Sep 26 19:09:17 EDT 1998 | Graham Naisbitt
As an addendum to Daves posting, please consider that: There is no such thing as no residue fluxing. A no-clean must herefore, have benign residues - in other words, they are not as efficient at removing surface oxides to enable good solder joints. S
Electronics Forum | Mon Jan 19 20:01:11 EST 1998 | Steve Gregory
| We use no clean paste and sometimes experience | flux splattering which gives spot on gold fingers. | Need help in analize the cause. thx. Dominic, That is STILL a problem huh? It's a tough one to solve sometimes...especially when you have as
Electronics Forum | Tue Aug 21 21:39:19 EDT 2001 | davef
1) why is No-clean (NC) the preferred process, for BGA mounting by SMT? Probably the same reason NC is the preferred process for mounting non-area array SMT components. 2) why is water-soluble (WS) not a hot choice? There�s not reason not to use
Electronics Forum | Mon Jun 07 12:22:44 EDT 1999 | Chrys Shea
| I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole." The
Electronics Forum | Tue Mar 10 22:16:56 EST 1998 | Steve Gregory
Jeremy, I'm gonna make a couple of assumptions by "reading in between the lines" of your email: 1. You're using no-clean paste. 2. This is only happening on the second side. You tell me if I'm wrong about this... First thing, if you're only experienc
Electronics Forum | Wed Sep 19 11:32:17 EDT 2001 | Mike Konrad
Hi Kevin, Sorry for the delay in responding to your question. I have been trapped in Australia (not a bad place to be trapped I may add). The scale in your cleaner is not usually caused by the chemical used in the wash cycle (although Armakleen ha
Electronics Forum | Mon Jul 24 15:10:37 EDT 2006 | carln
Here are some additional comments that have been posted on the CircuitNet web site: Fist, the answer is the same regardless of the specific paste type, (leaded or non-leaded). High pressure sprays should never be applied to a stencil. Stencils are