Electronics Forum | Tue Apr 09 05:10:39 EDT 2002 | sanchai
Dear sir, Do you have experiment about the temperature cycling and vibration test for reliability testing of surface mount solder attachment. If yes, please give me the soft file sample of parameter setting and testing report.. Thank you very mu
Electronics Forum | Tue Apr 09 08:27:55 EDT 2002 | davef
Read SM-785 - "Guidelines For Accelerated Reliability Testing Of SM Solder Attachments"
Electronics Forum | Wed Sep 29 02:16:37 EDT 2004 | FengAng
Hi all, Our department need to setup a reliability lab. And some equipments are need to purchase. At the first stage, thermal cycling test are going to be imported. If anyone of you have this kind of experience, please don't hesitate to SHARE me h
Electronics Forum | Fri Nov 04 08:29:13 EST 2005 | davef
There is no relationship between accelerated and actual life tests.
Electronics Forum | Wed Sep 29 06:20:14 EDT 2004 | Peppe
FengAng, I'm involved in similar activities on telecom products and we use as reference: MIL-STD-883E, JESD22, IEC-749. We have 2 climatic chamber to arrange a wide range of test, depending on customer use and/or specs. Based on that experience, we p
Electronics Forum | Fri Apr 24 20:33:06 EDT 1998 | D.Lange
| Looking for anyone who has experience with high temperature soldering. Need to determine why solder joints are failing. Thermocycling of unit is -40C to +140C, 30 minute dwell time, 10 sec. transition time | Your help is appreciated | Ed Holton |
Electronics Forum | Thu Dec 21 04:27:31 EST 2000 | teohbengee
Need help urgently. Anyone can provide me some information or site on reliability test on PCB assembly like solder joint or anything. Some test like ERSA Test, SHMOO Test, Pull Test, Temperature cycle and humidity Test, vibration Test or any related
Electronics Forum | Sun Apr 11 11:39:52 EDT 2010 | manchella
When we have sent some of motherboards for reliability testing in a tird party laoratory. It is found that when Dye&Pry is done after 600 cycles of Thermal Cycling, in LGA socket only one of the corner solder joing had 100% type 3 crack. All other so
Electronics Forum | Tue Apr 13 08:21:05 EDT 2010 | esca
Hi manchella, After ATC test, two different failure modes can be present: solder FATIGUE (into bulk) or BRITTLE INTERMETALLIC fracture. So, first you have to verify this. Moreover, which brand of SMT paste have you used ? The crack into solder joint
Electronics Forum | Tue Dec 19 07:58:29 EST 2006 | ccgooi
Our company is assembly flip chip on flex, we have new design of flip chip which die temperature will increase until 145 degree C after test run the end product, however the Tg,glass transition temperature is 148. Will this case causing any reliabil