Electronics Forum | Thu May 26 08:52:42 EDT 2011 | davef
Phil Zarrow wrote a useful paper that could help in evaluating paste. Here read it ... Evaluating Solder Paste � Not An Option Contributed by Phil Zarrow of ITM an Independent SMT consulting firm With soldering being the dominant source of assembly
Electronics Forum | Fri Jul 08 16:35:04 EDT 2005 | Jason Fullerton
"Whether or not you need a toe fillet depends on your application. We have high reliability products where we can't use a QFN over a certain size, regardless of toe fillet. We have other applications where we meet the thermal cycle requirements for a
Electronics Forum | Fri Sep 17 06:01:12 EDT 1999 | Earl Moon
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Fri Sep 17 03:55:45 EDT 1999 | Brian
| We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a reco
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Fri Sep 17 15:01:05 EDT 1999 | Dave F
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Sat Sep 18 13:05:57 EDT 1999 | Brian
| | | | | | Dave, I'll respond by paragraph: | | | | | | | Brian: | | | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slath
Electronics Forum | Sat Sep 18 14:37:00 EDT 1999 | Earl Moon
| | | | | | | | | Dave, I'll respond by paragraph: | | | | | | | | | Brian: | | | | | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like
Electronics Forum | Wed Dec 20 15:40:36 EST 2006 | slthomas
I'm no metallurgist but I don't think you're going to burn up lead with a soldering iron. That said, I would surmise that you could pull a lot of the metallization from the component terminations (very likely lead free) and the pads on the board (i