Hello SMTA. I'm having issues reworking QFNs inside housings with a much higher thermal mass than any typical PCB. We have had demonstrations in-house using BGA rework stations that simply don't get the job done. The problem is threefold: 1) th
Electronics Forum | Thu Sep 23 08:47:25 EDT 2021 | majdi4
1)Though in many cases the difference between SAC305 and SAC405 was small,and not always statistically significant, it was observed that SAC405 generally outperformed SAC305 joints. Under 0°C to 100°C thermal cycling,no statistically significant
Electronics Forum | Fri Jan 06 00:03:10 EST 2023 | SMTA-64419298
Hello Evtimov, sorry...just saw post as I was looking through list...a bit late. I don't know if you ever got your answer. IPC-4552A covers EniG finishes and suggested shelf life. I've referred to these doc's quite a bit. Good spec's ! Yes, I beli
Electronics Forum | Fri May 26 04:58:19 EDT 2023 | auriga2001
I agree with the two other replies. Left alone, it is a defect. If it's just excess adhesive or coating, you can use IPC-7711/7721 'Rework, Modification and Repair of Electronic Assemblies' for guidance on removing. Section 2.3.1 explains how to te
Electronics Forum | Fri Jun 23 12:30:24 EDT 2000 | Super K (Evil K)
To answer Gary's question: Gary, you will need a production board, thermal profiler, flux vendors product data sheet on the flux you intend to use, maybe your wave vendor service engineer or wave solder vendor contact (unless you know your wave) and
Electronics Forum | Fri Jun 23 12:32:20 EDT 2000 | Super K (Evil K)
To answer Gary's question: Gary, you will need a production board, thermal profiler, flux vendors product data sheet on the flux you intend to use, maybe your wave vendor service engineer or wave solder vendor contact (unless you know your wave) and
Electronics Forum | Fri Jun 25 16:54:25 EDT 1999 | C.K.
| | | Dear John/Earl | | | | | | Thanks for your clarifications. To me also the problem does not seem to be linked with the PCB. The Pre heater temp. is set at | | | 450 degree C. We are using Alpha Aq. cleanable flux. Can you elaborate on the
Electronics Forum | Wed May 12 10:29:25 EDT 1999 | Timothy O'Neill
| | | Can anyone tell me what the recommended "typical" cooling rates are after reflow? Are the cooling rates considered as critical to control as the heating rates and why/why not? | | | I do not think there is a "typical" post reflow cooling rate
Electronics Forum | Tue Oct 27 16:11:36 EST 1998 | carl m
| | | | What are the key feature to look for in buying a profiling product for Reflow ? | | | | | | Who's is the best and how much do these systems cost ? | | | | | | Thanks in advance. | | | | | | Hi Mark, | | | | I am currently the oven secto
Electronics Forum | Tue May 26 17:29:42 EDT 1998 | Earl Moon
| I know, I've read the "been there done that" stories about this subject, but I still profess ignorance on some aspects. | We are using NPO type dialectric caps in potted high voltage assemblies and continue to experience catastrophic vailures. U